| 1. |
- Almjashev, V.I., et al.
(författare)
-
Eutectic crystallization in the FeO(1.5)-UO(2+x)-ZrO(2) system
- 2009
-
Ingår i: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 389:1, s. 52-56
-
Tidskriftsartikel (refereegranskat)abstract
- Results of the investigation of the FeO(1.5)-UO(2+x)-ZrO(2) system in air are presented. The eutectic position and the content of the phases crystallized at this point have been determined. The temperature and the composition of the ternary eutectic are 1323 +/- 7 degrees C and 67.4 +/- 1.0 FeO(1.5), 30.5 +/- 1.0 UO(2+x), 2.1 +/- 0.2 ZrO(2) mol.%, respectively. The solubilities of FeO(1.5) and ZrO(2) in the UO(2+x)(FeO(1.5), ZrO(2)) solid solution correspond to respectively 3.2 and 1.1 mol.%. The solubilities of UO(2) and ZrO(2) in FeO(1.5) are not significant. The existence of a solid solution on the basis of U(Zr)FeO(4) compound is found. The ZrO(2) Solubility in this solid solution is 7.0 mol.%.
|
|
| 2. |
- Almjashev, V.I., et al.
(författare)
-
Phase equilibria in the FeO(1+x)-UO(2)-ZrO(2) system in the FeO(1+x)-enriched domain
- 2010
-
Ingår i: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 400:2, s. 119-126
-
Tidskriftsartikel (refereegranskat)abstract
- Experimental results of the investigation of the FeO(1+x)UO(2)-ZrO(2) system in neutral atmosphere are presented. The ternary eutectic position and the composition of the phases crystallized at this point have been determined. The phase diagram is constructed for the FeO(1+x)-enriched region and the onset melting temperature of 1310 degrees C probably represents a local minimum and so will be a determining factor in this system and its application to safety studies in nuclear reactors.
|
|
| 3. |
- Almjashev, V.I., et al.
(författare)
-
Ternary eutectics in the systems FeO-UO2-ZrO2 and Fe2O3-U3O8-ZrO21
- 2011
-
Ingår i: Radiochemistry. - 1066-3622. ; 53:1, s. 13-18
-
Tidskriftsartikel (refereegranskat)abstract
- The systems FeO–UO2–ZrO2 (in inert atmosphere) and Fe2O3–U3O8–ZrO2 (in air) were studied. Forthe FeO–UO2–ZrO2 system, the eutectic temperature was found to be 1310°С, with the following componentconcentrations (mol %): 91.8 FeO, 3.8 UO2, and 4.4 ZrO2. For the Fe2O3–U3O8–ZrO2 system, the eutectictemperature was found to be 1323°С, with the following component concentrations (mol %): 67.4 FeO1.5,30.5 UO2.67, and 2.1 ZrO2. The solubility limits of iron oxides in the phases based on UO2(ZrO2,FeO) andUO2.67(ZrO2,FeO1.5) were determined
|
|
| 4. |
- Bakardjieva, S., et al.
(författare)
-
Improvement of the European thermodynamic database NUCLEA
- 2010
-
Ingår i: Progress in nuclear energy (New series). - : Elsevier BV. - 0149-1970 .- 1878-4224. ; 52:1, s. 84-96
-
Tidskriftsartikel (refereegranskat)abstract
- Modelling of corium behaviour during a severe accident requires knowledge of the phases present at equilibrium for a given corium composition, temperature and pressure. The thermodynamic database NUCLEA in combination with a Gibbs Energy minimizer is the European reference tool to achieve this goal. This database has been improved thanks to the analysis of bibliographical data and to EU-funded experiments performed within the SARNET network, PLINIUS as well as the ISTC CORPHAD and EVAN projects. To assess the uncertainty range associated with Energy Dispersive X-ray analyses, a round-robin exercise has been launched in which a UO2-containing corium-concrete interaction sample from VULCANO has been analyzed by three European laboratories with satisfactorily small differences.
|
|
| 5. |
- Bakardjieva, S., et al.
(författare)
-
Improvement of the European thermodynamic database NUCLEA in the frame of EU-funded experiments
- 2008
-
Ingår i: Proceedings of the 3<sup>rd</sup> European Review Meeting on Severe Accident Research (ERMSAR 2008).
-
Konferensbidrag (refereegranskat)abstract
- Modelling of corium behaviour during a severe accident requires knowledge of the phases present at equilibrium for a given corium composition, temperature and pressure. The thermodynamic database NUCLEA in combination with a Gibbs Energy minimizer is theEuropean reference tool to achieve this goal. Within SARNET, this database has beenimproved thanks to the analysis of bibliographical data and to EU0funded experimentsperformed within the SARNET network, PLINIUS as well as the ISTC CORPHAD and EVAN projects. To assess the uncertainty range associated with Energy Dispersive X-ray analyses, a round robin exercise has been launched in which a UO2-containing coriumconcrete interaction sample from VULCANO has been analyzed by three European laboratories with satisfactorily small differences.
|
|
| 6. |
- Bechta, Sevostian, et al.
(författare)
-
Corium phase equilibria based on MASCA, METCOR and CORPHAD results
- 2008
-
Ingår i: Nuclear Engineering and Design. - : Elsevier BV. - 0029-5493 .- 1872-759X. ; 238:10, s. 2761-2771
-
Tidskriftsartikel (refereegranskat)abstract
- Experimental data on component partitioning between suboxidized corium melt and steel in the invessel melt retention (IVR) conditions are compared. The data are produced within the OECD MASCAprogram and the ISTC CORPHAD project under close-to-isothermal conditions and in the ISTC METCORproject under thermal gradient conditions. Chemical equilibrium in the U–Zr–Fe(Cr,Ni,. . .)–O system isreached in all experiments. In MASCA tests the molten pool formed under inert atmosphere has twoimmiscible liquids, oxygen-enriched (oxidic) and oxygen-depleted (metallic), resulting of the miscibilitygap of the mentioned system. Sub-system data of the U–Zr–Fe(Cr,Ni,. . .)–O phase diagram investigatedwithin the ISTC CORPHAD project are interpreted in relation with the MASCA results. In METCOR teststhe equilibrium is established between oxidic liquid and mushy metallic part of the system. Results ofcomparison are discussed and the implications for IVR noted.
|
|
| 7. |
- Bechta, Sevostian, et al.
(författare)
-
CORPHAD and METCOR ISTC projects
- 2005
-
Ingår i: Proceedings of The first European Review Meeting on Severe Accident Research (ERMSAR-2005).
-
Konferensbidrag (refereegranskat)abstract
- The ongoing CORPHAD Project (Phase Diagrams for Multicomponent SystemsContaining Corium and Products of its Interaction with NPP Materials) started in August2001. The main aim of the project is to experimentally determine the relevantphysicochemical data on phase diagrams of binary, ternary, quaternary and prototypic multicomponent systems, which are important for analysis and modelling of a severe accident (SA)and efficient planning of severe accident management (SAM) measures. The data should bedirectly used for the European NUCLEA database development and validation. The followingsystems are in the focus of the project: (1) UO2 – FeO, (2) ZrO2 – FeO, (3) SiO2– Fe2O3, (4)UO2 – SiO2, (5) UO2 – ZrO2-FeO, (6) UO2 – ZrO2-FeOy, (7) U-O-Fe, (8) Zr-O-Fe, (9) U-OZr, (10) U-Zr-Fe-O, (11) complex corium mixtures.The experimentally determined data of the listed diagrams include: coordinates ofcharacteristic points (eutectics, peritectics and others); liquidus and solidus concentrationcurves; component solubility limits in the solid phase; tie line coordinates and temperatureconcentration regions of the miscibility gap. Different methodologies are used for the phasediagram study. Classical methods of thermal analysis, like DTA and DSC are combined withmethods specifically developed for corium studies.The METCOR project (Investigation of Corium Melt Interaction with NPP ReactorVessel Steel) started in April 1999. The objectives of the project are to qualify and to quantifyphysico-chemical phenomena of corium melt interaction with reactor vessel steel cooled fromthe outside. The variable parameters of the interaction tests are: oxygen potential in thesystem, corium composition, interaction interface temperature and heat flux from corium tosteel. The medium scale tests with corium mass of about 2 kg are carried out by using highfrequency induction heating of the corium melt in a cold crucible.The METCOR & CORPHAD work-packages are performed by Russian partners inclose collaboration with leading European scientific institutes in the area of corium researchas well as with the European nuclear industry.This paper briefly describes the results obtained in both projects and their possibleapplication for SA analysis and SAM. The paper concludes with recommendations for futureresearch activities in the framework of METCOR and CORPHAD projects.
|
|
| 8. |
- Bechta, Sevostian, et al.
(författare)
-
Phase diagram of the UO2-FeO1+x system
- 2007
-
Ingår i: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 362:1, s. 46-52
-
Tidskriftsartikel (refereegranskat)abstract
- Phase-relation studies of the UO2–FeO1+x system in an inert atmosphere are presented. The eutectic point has beendetermined, which corresponds to a temperature of (1335 ± 5) C and a UO2 concentration of (4.0 ± 0.1) mol.%. Themaximum solubility of FeO in UO2 at the eutectic temperature has been estimated as (17.0 ± 1.0) mol.%. Liquidus temperaturesfor a wide concentration range have been determined and a phase diagram of the system has been constructed.
|
|
| 9. |
- Bechta, Sevostian, et al.
(författare)
-
Phase diagram of the ZrO2-FeO system
- 2006
-
Ingår i: Journal of Nuclear Materials. - : Elsevier BV. - 0022-3115 .- 1873-4820. ; 348:1-2, s. 114-121
-
Tidskriftsartikel (refereegranskat)abstract
- The results on the ZrO2–FeO system studies in a neutral atmosphere are presented. The refined eutectic point has beenfound to correspond to a ZrO2 concentration of 10.3 ± 0.6 mol% at 1332 ± 5 C. The ultimate solubility of iron oxide inzirconia has been determined in a broad temperature range, taking into account the ZrO2 polymorphism. A phase diagramof the pseudobinary system in question has been constructed.
|
|
| 10. |
- Bechta, Sevostian, et al.
(författare)
-
Phase Relations in the ZrO2–FeO System
- 2006
-
Ingår i: Russian Journal of Inorganic Chemistry. - 0036-0236 .- 1531-8613. ; 51:2, s. 325-331
-
Tidskriftsartikel (refereegranskat)abstract
- We present the results of the investigation of the ZrO2-FeO system under an inert atmosphere. We have refined the position of the eutectic point, which lies at 1332 +/- 5 degrees C and 10.3 +/- 0.6 mol % ZrO2. The iron oxide solubility boundaries in zirconium dioxide have been determined over a wide temperature range taking into account the polymorphism in ZrO2. A phase diagram for the system has been designed.
|
|
| 11. |
- Bechta, Sevostian, et al.
(författare)
-
Phase transformation in the binary section of the UO2-FeO-Fe system
- 2007
-
Ingår i: Radiochemistry (New York, N.Y.). - 1066-3622 .- 1608-3288. ; 49:1, s. 20-24
-
Tidskriftsartikel (refereegranskat)abstract
- Phase transformations in the oxide binary section of the UO2-FeO-Fe ternary system were studied. The melting onset point of the UO2-FeO heterogeneous system (1335±5°C) was determined and the fusion curve of this system was constructed. The limiting solubility of FeO in the UO2 solid solution was measured. The changes in crystal parameters in formation of the solid solution were determined. Uranium dioxide was found to be insoluble in the wüstite phase (FeO).
|
|
| 12. |
- Mezentseva, L.P., et al.
(författare)
-
Phase and chemical transformations in the SiO2-Fe2O3(Fe3O4) system at various oxygen partial pressures
- 2006
-
Ingår i: Russian Journal of Inorganic Chemistry. - 0036-0236 .- 1531-8613. ; 51:1, s. 118-125
-
Tidskriftsartikel (refereegranskat)abstract
- The SiO2-Fe2O3(F3O4) system has been studied in air, oxygen, and an inert atmosphere. The dissociation temperatures for iron oxides, the onset and full melting temperatures for coexisting phases, and the melt demixing temperatures have been determined as a function of the oxygen partial pressure. A scenario of the phase and chemical transformations in the title systems has been developed.
|
|