- Bonin, Pierre, et al.
(författare)
-
Impedance analysis of the barrier effect of coil-coated materials : Water uptake and glass transition variations
- 2021
-
Ingår i: Progress in organic coatings. - : Elsevier B.V.. - 0300-9440 .- 1873-331X. ; 153
-
Tidskriftsartikel (refereegranskat)abstract
- In the present work, an industrial polyester coil-coated steel sample was characterized by electrochemical impedance spectroscopy. The diagrams were obtained for various immersion times in a 0.5 M NaCl solution for three different initial states of the same coil coating (as received, dried and dried after the impedance measurements). The aim of the study was to have a better knowledge of how the water uptake influences the coil coating physical properties and to extract relevant parameters of the ageing processes. From the high-frequency part of the impedance diagrams, the water uptake was calculated using a linear rule of mixtures. Two sorption regions were observed for the dried samples suggesting the presence of porosities already filled with ambient moisture for the as-received sample. It was shown that the water uptake was a slow process and, independently of the initial state of the sample, a saturation plateau was never reached, even after 456 h of immersion. A time constant, clearly visible on the phase angle of the impedance diagrams, was analysed through the dielectric permittivity formalism and attributed to the signature of the dielectric manifestation of the glass transition. This time constant was shifted to higher frequencies with increasing water fraction (increasing immersion time), consistent with a plasticization effect. This result was supported by differential scanning calorimetry measurements. Finally, the data obtained for the different initial states of the coating highlighted that, even if the water uptake was reversible, the sorption kinetics was different for the sample dried after the impedance measurements. This could be of importance in the degradation process of the coil coated steel.
|
|
| 2. |
- Caussé, Nicolas, et al.
(författare)
-
Ageing processes of coil-coated materials : Temperature-controlled electrochemical impedance analysis
- 2023
-
Ingår i: Progress in organic coatings. - : Elsevier B.V.. - 0300-9440 .- 1873-331X. ; 183
-
Tidskriftsartikel (refereegranskat)abstract
- In the present work, an industrial polyester coil-coated steel was characterized by electrochemical impedance spectroscopy (EIS) during immersion in a 0.5 M NaCl solution for different temperatures (30, 40, 50 and 60 °C). The objective was to propose a methodology to follow the ageing of the coil-coated system, from the first stage of water uptake until the blistering appearance. Relevant parameters were extracted from the EIS diagrams to analyse ageing processes of the polymer and of the metal/polymer interface. Water uptake was determined from the high-frequency part of the impedance diagrams using a linear rule of mixtures. By increasing the temperature, both the water uptake kinetics and the water content in the coating increased. The effect of water uptake on the physical structure of the coating (plasticization) was discussed through the analysis of a time constant corresponding to the dielectric manifestation of the polymer glass transition. At 40, 50 and 60 °C, appearance of corrosion was detected on the impedance spectra by a decrease, at low frequency, of the impedance modulus and of the phase angle. For 60 °C, the corroded surface area as a function of time, was assessed from the EIS data analysis with adapted equivalent circuits. The corroded surface areas followed similar trend as blister surface areas determined from images analysis.
|
|