  • Moreno, Maiara, 1993-, et al. (författare)
  • Strain and phase evolution in TiAlN coatings during high-speed metal cutting : An in operando high-energy x-ray diffraction study
  • 2024
  • Ingår i: Acta Materialia. - : Elsevier. - 1359-6454 .- 1873-2453. ; 263
  • Tidskriftsartikel (refereegranskat)abstract
    • We report on phase and strain changes in Ti1-xAlxN (0 ≤ x ≤ 0.61) coatings on cutting tools during turning recorded in operando by high-energy x-ray diffractometry. Orthogonal cutting of AISI 4140 steel was performed with cutting speeds of 360–370 m/min. Four positions along the tool rake face were investigated as a function of time in cut. Formation of γ-Fe in the chip reveals that the temperature exceeds 727 °C between the tool edge and the middle of the contact area when the feed rate is 0.06 mm/rev. Spinodal decomposition and formation of wurtzite AlN occurs at the positions of the tool with the highest temperature for the x ≥ 0.48 coatings. The strain evolution in the chip reveals that the mechanical stress is largest closest to the tool edge and that it decreases with time in cut for all analyzed positions on the rake face. The strain evolution in the coating varies between coatings and position on the rake face of the tool and is affected by thermal stress as well as the applied mechanical stress. Amongst others, the strain evolution is influenced by defect annihilation and, for the coatings with highest Al-content (x ≥ 0.48), phase changes.
  •  
2.
  • Schramm Benítez, Isabella Citlalli (författare)
  • Defect-engineered (Ti,Al)N thin films
  • 2017
  • Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
    • This thesis investigates the effect of point defects (nitrogen vacancies and interstitials) and multilayering ((Ti,Al)N/TiN) on the phase transformations in cathodic arc-evaporated cubic (Ti,Al)N thin films at elevated temperatures. Special attention is paid to the evolution of the beneficial spinodal decomposition into c-TiN and c-AlN, the detrimental formation of wurtzite AlN and the potential application as hard coating in cutting tools.c-(Ti1-xAlx)Ny thin films with varying Al fractions and N content (y = 0.93 to 0.75) show a delay in the spinodal decomposition when increasing the amount of N vacancies. This results in a 300 °C upshift in the age hardening and a delay in the w-AlN formation, while additions of self-interstitials enhance phase separation. High temperature interaction between hard metal substrates and thin films is more pronounced when increasing N deficiency through diffusion of substrate elements into the film. Low N content films (y = 0.58 to 0.40) showed formation of additional phases such as Ti4AlN3, Ti2AlN, Al5Ti2 and Al3Ti during annealing and a transformation from Ti2AlN to Ti4AlN3 via intercalation. The multilayer structure of TiN/TiAlN results in surfacedirected spinodal decomposition that affects the decomposition behavior. Careful use of these effects appears as a promising method to improve cutting tool performance.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-2 av 2

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy