| 1. |
- Kaplan, Maciej, 1991-, et al.
(författare)
-
Combinatorial design of amorphous TaNiSiC thin films with enhanced hardness, thermal stability, and corrosion resistance
- 2022
-
Ingår i: Materials & design. - : Elsevier. - 0264-1275 .- 1873-4197. ; 220
-
Tidskriftsartikel (refereegranskat)abstract
- Amorphous TaNiSiC and TaNiC films (with varying Ta/Ni and Si/C ratios) were deposited using combinatorial magnetron sputtering. The TaNiSiC films remained X-ray amorphous after four hour-long annealings up to 700 °C, while TaNiC alloys with high Ni and C contents crystallized. These differences were attributed to a strong driving force for separation of Ni and C in TaNiC, whereas the addition of Si, due to its solubility in the other elements, reduced the elemental segregation in TaNiSiC. The as-deposited TaNiSiC films exhibited hardnesses of 9–12 GPa. Annealing led to an increase in hardness by 2–4 GPa, due to decreases in average atomic distance, as evidenced by X-ray diffraction measurements. Potentiodynamic polarizations from –0.7 to +1.5 V vs. Ag/AgCl (3 M NaCl) in 10 mM sodium borate showed lower current densities by up to 2 orders of magnitude with increasing Ta content (28–52 at.%). Changes in Si/C content (7–13 at.% Si) had no effect. However, optical microscopy showed that TaNiSiC films with high Si/low C contents (13/10 at.%) suffered much less localized etching compared to TaNiC films. Thus, Si had a significant role in increasing the mechanical strength, corrosion resistance, and thermal stability of the TaNiSiC films.
|
|
| 2. |
- Srinath, Aishwarya, 1991-, et al.
(författare)
-
An investigation of the corrosion resistances of magnetron sputtered TaW-rich, Nb-rich, and multicomponent CrNbTaTiW alloys
-
Annan publikation (övrigt vetenskapligt/konstnärligt)abstract
- The corrosion resistances of magnetron sputtered nearequimolar, TaW-rich, and Nb-rich CrNbTiTaW alloys, with and without 8 at.% carbon, were studied in aqueous chloride-containing environments. Electrochemical tests and scanning electron images showed that all the CrNbTaTiW alloys were highly corrosion resistant in 1.0 M HCl. The results conclusively showed that passivated nearequimolar CrNbTaTiW coatings have comparable corrosion performances to passivated Nb- and TaW-rich alloys in 0.01 M HCl + 0.1 M NaCl. Carbon affected the rate of surface repassivation in polarisation measurements of the films whose oxide had been partially reduced, but had a minor influenceon the corrosion resistances once a mature oxide was formed. No conclusive relationships between microstructure and corrosion resistance were established. The comparable corrosion resistances of the multicomponent CrNbTiTaW, Nb-rich and TaW-rich alloys were attributed to the presence of extremely stable surface oxides of Nb and Ta which prevented losses of Ti and Cr. The near surface regions of all the alloys before and after corrosion appeared to be depleted in W compared to the bulk.
|
|
| 3. |
|
|