Träfflista för sökning "WFRF:(Tengdelius Lina 1986 ) "

Sökning: WFRF:(Tengdelius Lina 1986 )

  • Resultat 1-7 av 7
Sortera/gruppera träfflistan
   
NumreringReferensOmslagsbildHitta
1.
  • Engberg, David L. J., 1986-, et al. (författare)
  • Atom probe tomography field evaporation characteristics and compositional corrections of ZrB2
  • 2019
  • Ingår i: Materials Characterization. - : Elsevier BV. - 1044-5803 .- 1873-4189. ; 156
  • Tidskriftsartikel (refereegranskat)abstract
    • The microstructure of stoichiometric ZrB2.0 and B over-stoichiometric ZrB2.5 thin films has been studied using atom probe tomography (APT), X-ray diffraction, and transmission electron microscopy. Both films consist of columnar ZrB2 grains with AlB2-type crystal structure. The narrow stoichiometry range of ZrB2 results in the presence of separate disordered B-rich boundaries even in ZrB2.0. At higher average B content, specifically ZrB2.5, the formation of a continuous network around the sides of the ZrB2 columns is promoted. In addition, the APT field evaporation characteristics of ZrB2 and its influence on the measured local composition has been studied and compared to the average composition from elastic recoil detection analysis (ERDA). Differences in the measured average compositions of the two techniques are explained by the APT detector dead-time/space. A new pile-up pairs correction procedure based on co-evaporation correlation data was thus employed here for the APT data and compared with the 10B-method (the B equivalence of the 13C-method), as well as the combination of both methods. In ZrB2.0, all of the applied compositional correction methods were found to reduce the compositional difference when appropriate isotopic abundances were used. In ZrB2.5, the inhomogeneity of the film likely increased the local APT composition to such an extent that even conservative correction procedures overestimated the B content compared to the ERDA reference. The strengths of the pile-up pairs correction compared the 10B and the combined methods are higher precision, due to it being less dependent on the accuracy of estimated isotopic abundances, and that the correction itself is not dependent on careful background correction of the mass spectrum.
  •  
2.
  • Magnuson, Martin, 1965-, et al. (författare)
  • ­Chemical Bonding in Epitaxial ZrB2 Studied by X-ray Spectroscopy
  • 2018
  • Ingår i: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 649, s. 89-96
  • Tidskriftsartikel (refereegranskat)abstract
    • The chemical bonding in an epitaxial ZrB2 film is investigated by Zr K-edge (1s) X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopies and compared to the ZrB2 compound target from which the film was synthesized as well as a bulk α-Zr reference. Quantitative analysis of X-ray Photoelectron Spectroscopy spectra reveals at the surface: ~5% O in the epitaxial ZrB2 film, ~19% O in the ZrB2 compound target and ~22% O in the bulk α-Zr reference after completed sputter cleaning. For the ZrB2 compound target, X-ray diffraction (XRD) shows weak but visible   11, 111, and 220 peaks from monoclinic ZrO2 together with peaks from ZrB2 and where the intensity distribution for the ZrB2 peaks show a randomly oriented target material.  For the bulk α-Zr reference no peaks from any crystalline oxide were visible in the diffractogram recorded from the 0001-oriented metal. The Zr K-edge absorption from the two ZrB2 samples demonstrate more pronounced oscillations for the epitaxial ZrB2 film than in the bulk ZrB2 attributed to the high atomic ordering within the columns of the film. The XANES exhibits no pre-peak due to lack of p-d hybridization in ZrB2, but with a chemical shift towards higher energy of 4 eV in the film and 6 eV for the bulk compared to α-Zr (17.993 keV) from the charge-transfer from Zr to B. The 2 eV larger shift in bulk ZrB2 material suggests higher oxygen content than in the epitaxial film, which is supported by XPS. In EXAFS, the modelled cell-edge in ZrB2 is slightly smaller in the thin film (a=3.165 Å, c=3.520 Å) in comparison to the bulk target material (a=3.175 Å, c=3.540 Å) while in hexagonal closest-packed metal (α-phase, a=3.254 Å, c=5.147 Å). The modelled coordination numbers show that the EXAFS spectra of the epitaxial ZrB2 film is highly anisotropic with strong in-plane contribution, while the bulk target material is more isotropic. The Zr-B distance in the film of 2.539 Å is in agreement with the calculated value from XRD data of 2.542 Å. This is slightly shorter compared to that in the ZrB2 compound target 2.599 Å, supporting the XANES results of a higher atomic order within the columns of the film compared to bulk ZrB2.
  •  
3.
  • Magnuson, Martin, 1965-, et al. (författare)
  • Compositional dependence of epitaxial Tin+1SiCn MAX-phase thin films grown from a Ti3SiC2 compound target
  • 2019
  • Ingår i: Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films. - : American Institute of Physics (AIP). - 0734-2101 .- 1520-8559. ; 37:2
  • Tidskriftsartikel (refereegranskat)abstract
    • The authors investigate sputtering of a Ti3SiC2 compound target at temperatures ranging from RT (no applied external heating) to 970 °C as well as the influence of the sputtering power at 850 °C for the deposition of Ti3SiC2 films on Al2O3(0001) substrates. Elemental composition obtained from time-of-flight energy elastic recoil detection analysis shows an excess of carbon in all films, which is explained by differences in the angular distribution between C, Si, and Ti, where C scatters the least during sputtering. The oxygen content is 2.6 at. % in the film deposited at RT and decreases with increasing deposition temperature, showing that higher temperatures favor high purity films. Chemical bonding analysis by x-ray photoelectron spectroscopy shows C–Ti and Si–C bonding in the Ti3SiC2 films and Si–Si bonding in the Ti3SiC2 compound target. X-ray diffraction reveals that the phases Ti3SiC2, Ti4SiC3, and Ti7Si2C5 can be deposited from a Ti3SiC2 compound target at substrate temperatures above 850 °C and with the growth of TiC and the Nowotny phase Ti5Si3Cx at lower temperatures. High-resolution scanning transmission electron microscopy shows epitaxial growth of Ti3SiC2, Ti4SiC3, and Ti7Si2C5 on TiC at 970 °C. Four-point probe resistivity measurements give values in the range ∼120 to ∼450 μΩ cm and with the lowest values obtained for films containing Ti3SiC2, Ti4SiC3, and Ti7Si2C5.
  •  
4.
  • Magnuson, Martin, 1965-, et al. (författare)
  • Reactive magnetron sputtering of tungsten target in krypton/trimethylboron atmosphere
  • 2019
  • Ingår i: Thin Solid Films. - : Elsevier. - 0040-6090 .- 1879-2731. ; 688
  • Tidskriftsartikel (refereegranskat)abstract
    • W-B-C films were deposited on Si(100) substrates held at elevated temperature by reactive sputtering from a W target in Kr/trimethylboron (TMB) plasmas. Quantitative analysis by Xray photoelectron spectroscopy (XPS) shows that the films are W-rich between ~ 73 and ~ 93 at.% W. The highest metal content is detected in the film deposited with 1 sccm TMB. The C and B concentrations increase with increasing TMB flow to a maximum of ~18 and ~7 at.%, respectively, while the O content remains nearly constant at 2-3 at.%. Chemical bonding structure analysis performed after samples sputter-cleaning reveals C-W and B-W bonding and no detectable W-O bonds. During film growth with 5 sccm TMB and 500 o C or with 10 sccm TMB and 300-600 o C thin film X-ray diffraction shows the formation of cubic 100-oriented WC1-x with a possible solid solution of B. Lower flows and lower growth temperatures favor growth of W and W2C, respectively. Depositions at 700 and 800 o C result in the formation of WSi2 due to a reaction with the substrate. At 900 o C, XPS analysis shows ~96 at.% Si in the film due to Si interdiffusion. Scanning electron microscopy images reveal a fine-grained microstructure for the deposited WC1-x films. Nanoindentation gives hardness values in the range from ~23 to ~31 GPa and reduced elastic moduli between ~220 and 280 GPa in the films deposited at temperatures lower than 600 o C. At higher growth temperatures the hardness decreases by a factor of 3 to 4 following the formation of WSi2 at 700-800 o C and Si-rich surface at 900 o C.
  •  
5.
  • Serban, Alexandra, 1988-, et al. (författare)
  • Magnetron Sputter Epitaxy of High-Quality GaN Nanorods on Functional and Cost-Effective Templates/Substrates
  • 2017
  • Ingår i: Energies. - Basel, Switzerland : MDPI AG. - 1996-1073. ; 10:9
  • Tidskriftsartikel (refereegranskat)abstract
    • We demonstrate the versatility of magnetron sputter epitaxy by achieving high-quality GaN nanorods on different substrate/template combinations, specifically Si, SiC, TiN/Si, ZrB2/Si, ZrB2/SiC, Mo, and Ti. Growth temperature was optimized on Si, TiN/Si, and ZrB2/Si, resulting in increased nanorod aspect ratio with temperature. All nanorods exhibit high purity and quality, proved by the strong bandedge emission recorded with cathodoluminescence spectroscopy at room temperature as well as transmission electron microscopy. These substrates/templates are affordable compared to many conventional substrates, and the direct deposition onto them eliminates cumbersome post-processing steps in device fabrication. Thus, magnetron sputter epitaxy offers an attractive alternative for simple and affordable fabrication in optoelectronic device technology.
  •  
6.
  • Tengdelius, Lina, 1986- (författare)
  • Growth and Characterization of ZrB2 Thin Films
  • 2013
  • Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
    • In this thesis, growth of ZrB2 thin films by direct current magnetron sputtering is investigatedusing a high vacuum industrial scale deposition system and an ultra-high vacuum laboratory scalesystem. The films were grown from ZrB2 compound targets at temperatures ranging from ambient (without external heating) to 900 °C and with substrate biases from -20 to -120 V. Short deposition times of typically 100 or 300 s and high growth rates of 80-180 nm/min were emphasized to yield films with thicknesses of 300-400 nm. The films were characterized by thinfilm X-ray diffraction with the techniques θ/2θ and ω scans, pole figure measurements andreciprocal space mapping, scanning and transmission electron microscopy, elastic recoil detection analysis and four point probe measurements. The substrates applied were Si(100), Si(111),4H-SiC(0001) and GaN(0001) epilayers grown on 4H-SiC. The Si(111), 4H-SiC(0001) substrates and GaN(0001) epilayers were chosen given their small lattice mismatches to ZrB2 making them suitable for epitaxial growth.The films deposited in the industrial system were found to be close to stoichiometric with a low degree of contaminants, with O being the most abundant at a level of < 1 at.%. Furthermore, the structure of the films is temperature dependent as films deposited in this system without external heating are fiber textured with a 0001-orientation while the films deposited at 550 °C exhibitrandom orientation. In contrast, epitaxial growth was demonstrated in the laboratory scale system on etched 4H-SiC(0001) and Si(111) deposited at 900 °C following outgassing of the substrates at 300 °C and in-situ heat treatment at the applied growth temperature to remove the native oxides. However, films grown on GaN(0001) were found to be 0001 textured at the applied deposition conditions, which make further studies necessary to enable epitaxial growth on this substrate material. Four point probe measurements on the films deposited in the industrial system show typical resistivity values ranging from ˜95 to 200 μΩcm with a trend to lower values for the films deposited at higher temperatures and at higher substrate bias voltages.
  •  
7.
  • Tengdelius, Lina, 1986- (författare)
  • ZrB2 Thin Films : Growth and Characterization
  • 2016
  • Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
    • Zirconium diboride, ZrB2, is a ceramic material with bulk properties such as high melting point (3245 °C), high hardness (23 GPa), and low resistivity (~8 μΩcm). Thin film growth of ZrB2 using physical vapor deposition has suffered from problems with films deviating from stoichiometry and with high levels of contaminants, especially high oxygen content. The homogeneity range of ZrB2 is very narrow, and consequently it is vital to achieve the correct stoichiometry to grow films with high crystalline order.This thesis describes a direct current magnetron sputtering process to grow stoichiometric ZrB2 thin films with a low degree of impurities. Growth of epitaxial ZrB2 films was achieved on 4H-SiC(0001), Si(111) and Al2O3(0001) substrates. The effect of deposition temperature and power applied on the sputtering target was investigated and showed that high power density (8.77 Wcm-2) and high temperature (900 °C) resulted in films with the best composition and the highest crystal quality. ZrB2 films on GaN(0001) templates exhibit an amorphous layer at the film-substrate interface and the resulting films are either polycrystalline or textured.Resistivity measurements showed that the ZrB2 thin films exhibit typical resistivity values of ~100-250 μΩcm and that the resistivity decreased with increasing deposition temperature.Nanoindentation was applied to assess the mechanical properties of the films. The epitaxial ZrB2 films exhibit high elastic recovery and a hardness of ~45-50 GPa, twice as high as the literature bulk value. In addition, evaluation of the mechanical properties was performed at high temperatures of up to 600 °C and showed that the epitaxial films retained a higher hardness, compared to textured ZrB2 films and bulk, also at these temperatures.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-7 av 7

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy