  • Landälv, Ludvig, 1982-, et al. (författare)
  • Phase evolution of radio frequency magnetron sputtered Cr-rich (Cr,Zr)(2)O-3 coatings studied by in situ synchrotron X-ray diffraction during annealing in air or vacuum
  • 2019
  • Ingår i: Journal of Materials Research. - : CAMBRIDGE UNIV PRESS. - 0884-2914 .- 2044-5326. ; 34:22, s. 3735-3746
  • Tidskriftsartikel (refereegranskat)abstract
    • The phase evolution of reactive radio frequency (RF) magnetron sputtered Cr0.28Zr0.10O0.61 coatings has been studied by in situ synchrotron X-ray diffraction during annealing under air atmosphere and vacuum. The annealing in vacuum shows t-ZrO2 formation starting at similar to 750-800 degrees C, followed by decomposition of the alpha-Cr2O3 structure in conjunction with bcc-Cr formation, starting at similar to 950 degrees C. The resulting coating after annealing to 1140 degrees C is a mixture of t-ZrO2, m-ZrO2, and bcc-Cr. The air-annealed sample shows t-ZrO2 formation starting at similar to 750 degrees C. The resulting coating after annealing to 975 degrees C is a mixture of t-ZrO2 and alpha-Cr2O3 (with dissolved Zr). The microstructure coarsened slightly during annealing, but the mechanical properties are maintained, with no detectable bcc-Cr formation. A larger t-ZrO2 fraction compared with alpha-Cr2O3 is observed in the vacuum-annealed coating compared with the air-annealed coating at 975 degrees C. The results indicate that the studied pseudo-binary oxide is more stable in air atmosphere than in vacuum.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-1 av 1

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy