- Guerrini, Niccolo, et al.
(author)
-
Charging Mechanism of Li2MnO3
- 2020
-
In: Chemistry of Materials. - : AMER CHEMICAL SOC. - 0897-4756 .- 1520-5002. ; 32:9, s. 3733-3740
-
Journal article (peer-reviewed)abstract
- Operando mass spectroscopy demonstrates quantitatively that lithium extraction from Li2MnO3 is charge compensated by oxygen loss (O-loss) not oxidation of oxide ions that are retained within the structural framework (O-redox). This fact is confirmed by X-ray absorption and emission spectroscopy. Li NMR shows that the two-phase core-shell structure, which forms on charging, is composed of an intact Li2MnO3 core and a highly disordered shell containing no Li, with a composition close to MnO2. Discharge involves Li insertion into the disordered shell. CO2 and O-2 are detected on charging at 15 mA g(-1), whereas charging by galvanostatic intermittent titration technique (GITT) forms only CO2; an observation in agreement with the previously described model of oxygen evolution from high-voltage cathodes producing singlet O-2 that reacts with the electrolyte forming CO2. The dominance of oxygen evolution over O-redox is in accordance with the model of O-loss occurring when the oxide ions are undercoordinated; O in the shell devoid of Li is coordinated by only 2 Mn.
|
|