1. |
- Andersson, Joel, 1981-, et al.
(author)
-
Effect of Different Solution Heat Treatments on the Hot Ductility of Superalloys : Part 3 - Waspaloy
- 2013
-
In: Materials Science and Technology. - 0267-0836 .- 1743-2847. ; 29:1, s. 43-53
-
Journal article (peer-reviewed)abstract
- The susceptibility to heat affected zone cracking of Waspaloy has been investigated in terms of its hot ductility, measured as the reduction of area (RA). Gleeble testing with on-heating as well as on-cooling test cycles was carried out to illuminate the influence of different 4 h solution heat treatments between 996 and 1080°C. A ductility maximum of between 80 and 90%RA was found at 1050–1100°C for all conditions in the on-heating tests. Although the different heat treatment conditions showed similar macrohardness, the particle size and distribution of the γ′ and M23C6 phases differed, which significantly affected the on-heating ductility in the lower temperature test region. The ductile to brittle transition was initiated at 1100°C in the on-heating testing with indications of grain boundary liquation at the higher test temperatures. Ductility recovery, as measured in the on-cooling tests from 1240°C, was very limited with <30%RA for all conditions and test temperatures except for the 1080°C/4 h treatment, which exhibited 60%RA at 980°C.
|
|