1.	Chen, Song, et al. (author) Synthesis of calcium phosphate crystals with thin nacreous structure 2016 In: CrystEngComm. - : Royal Society of Chemistry. - 1466-8033. ; 18:6, s. 1064-1069 Journal article (peer-reviewed)abstract Nacre-like structures have attracted great interest in recent years due to their outstanding toughness, stiffness and impact resistance. However, there is a challenge associated with engineering nacre-like calcium phosphate crystals. In this study, thin nacreous-like monetite sheets were synthesized in solutions guided by a surfactant. The influence of temperature, initial pH, Ca/P ratio, stirring time and the concentration of cetyltrimethylammonium bromide (CTAB) on the nacre-like structure has been studied. Findings showed that a nacre-like structure could only be formed at a high temperature (90 °C), high initial pH (11), sufficient stirring time (3 h), and under the presence of CTAB. A small-angle X-ray scattering experiment carried out at a synchrotron radiation facility showed that the distance between nanolayers was around 2.6 nm and TEM confirmed the fine sheet-like structure. The mechanism of the formation the nacre-like structure and its characterization were discussed.

Chen, Song, et al. (author)
Synthesis of calcium phosphate crystals with thin nacreous structure
2016
In: CrystEngComm. - : Royal Society of Chemistry. - 1466-8033. ; 18:6, s. 1064-1069
Journal article (peer-reviewed)abstract
- Nacre-like structures have attracted great interest in recent years due to their outstanding toughness, stiffness and impact resistance. However, there is a challenge associated with engineering nacre-like calcium phosphate crystals. In this study, thin nacreous-like monetite sheets were synthesized in solutions guided by a surfactant. The influence of temperature, initial pH, Ca/P ratio, stirring time and the concentration of cetyltrimethylammonium bromide (CTAB) on the nacre-like structure has been studied. Findings showed that a nacre-like structure could only be formed at a high temperature (90 °C), high initial pH (11), sufficient stirring time (3 h), and under the presence of CTAB. A small-angle X-ray scattering experiment carried out at a synchrotron radiation facility showed that the distance between nanolayers was around 2.6 nm and TEM confirmed the fine sheet-like structure. The mechanism of the formation the nacre-like structure and its characterization were discussed.

Träfflista för sökning "id:"swepub:oai:DiVA.org:kth-180732" "