Phosphorus removal performance and speciation in virgin and modified argon oxygen decarburisation slag designed for wastewater treatment
- 2015
-
In: Water Research. - : Elsevier. - 0043-1354 .- 1879-2448. ; 87, s. 271-281
-
Journal article (peer-reviewed)abstract
- Argon oxygen decarburisation (ADD) slag may be used for phosphorus (P) removal, as its high pH and weatherable calcium (Ca) minerals provide sufficient Ca2+ and OH- for calcium phosphate (Ca-PO4) precipitation. This study examined the P removal performance of AOD slag for use as wastewater treatment material. Batch experiments were carried out using both synthetic P solution and real wastewater, followed by chemical modelling and X-ray absorption near edge structure (XANES) spectroscopy. The influences of initial P concentration, slag dose and modification by polyethylene glycol (PEG), an effective agent for generation of porous materials, were investigated to determine the optimal conditions for P removal by AOD slag. It was found that virgin AOD slag removed 94.8% of P from a synthetic P solution in 4 h and 97.8% in 10 h. This high P removal was accompanied by a rapid increase in pH from 7.0 to 10.74. The maximum P removal capacity (PRC) from synthetic P solution ranged from 1.3 to 27.5 mg P g(-1). The optimal AOD dose for P removal from wastewater, determined in 8-h batch experiments, was 25 g L-1. PEG modification increased the reaction rate and resulted in higher final pH, increasing PRC by 47.9%. Combined Visual MINTEQ and XANES analysis for detailed examination of P removal mechanisms revealed that the main P removal mechanism was precipitation of calcium phosphate. According to the XANES analysis, the main Ca-PO4 precipitate formed on virgin AOD slag under low initial P concentration and high pH was apatite, while brushite was the dominant product at high initial P concentration and low pH.
|
|