1.	Singhal, Sonal, et al. (författare) Photoluminescence measurements in the phase transition region of Zn1-x Cd (x) S films 2010 Ingår i: Journal of nanoparticle research. - : Springer Science and Business Media LLC. - 1388-0764 .- 1572-896X. ; 12:4, s. 1415-1421 Tidskriftsartikel (refereegranskat)abstract Thin films of Zn1-x Cd (x) S (0.1 a parts per thousand currency sign x a parts per thousand currency sign 0.5) were prepared by using pulsed laser ablation technique on corning glass substrates. Phase transition from cubic to hexagonal in Zn1-x Cd (x) S films is determined by X-ray diffraction analysis. We observed a lowering in the phase transition temperature with increase in the cadmium concentration. Transmission electron microscopy suggests the crystalline nature of thin films with average particle size of 15 nm. The grown Zn1-x Cd (x) S samples show the high peak intensity ratio of the near band edge emission to the defect center luminescence even at room temperature, which indicates the small concentration of complex defects in the samples. Photoluminescence measurement show stoichiometric dependence of the energy band gap and is found to have quadratic dependence on x.

Singhal, Sonal, et al. (författare)
Photoluminescence measurements in the phase transition region of Zn1-x Cd (x) S films
2010
Ingår i: Journal of nanoparticle research. - : Springer Science and Business Media LLC. - 1388-0764 .- 1572-896X. ; 12:4, s. 1415-1421
Tidskriftsartikel (refereegranskat)abstract
- Thin films of Zn1-x Cd (x) S (0.1 a parts per thousand currency sign x a parts per thousand currency sign 0.5) were prepared by using pulsed laser ablation technique on corning glass substrates. Phase transition from cubic to hexagonal in Zn1-x Cd (x) S films is determined by X-ray diffraction analysis. We observed a lowering in the phase transition temperature with increase in the cadmium concentration. Transmission electron microscopy suggests the crystalline nature of thin films with average particle size of 15 nm. The grown Zn1-x Cd (x) S samples show the high peak intensity ratio of the near band edge emission to the defect center luminescence even at room temperature, which indicates the small concentration of complex defects in the samples. Photoluminescence measurement show stoichiometric dependence of the energy band gap and is found to have quadratic dependence on x.