1.	Darakchieva, Vanya, et al. (författare) Role of impurities and dislocations for the unintentional n-type conductivity in InN 2009 Ingår i: PHYSICA B-CONDENSED MATTER. - : Elsevier BV. - 0921-4526. ; 404:22, s. 4476-4481 Tidskriftsartikel (refereegranskat)abstract We present a study on the role of dislocations and impurities for the unintentional n-type conductivity in high-quality InN grown by molecular beam epitaxy. The dislocation densities and H profiles in films with free electron concentrations in the low 10(17) cm(-1) and mid 10(18) cm(-3) range are measured, and analyzed in a comparative manner. It is shown that dislocations alone could not account for the free electron behavior in the InN films. On the other hand, large concentrations of H sufficient to explain, but exceeding substantially, the observed free electron densities are found. Furthermore, enhanced concentrations of H are revealed at the film surfaces, resembling the free electron behavior with surface electron accumulation. The low-conductive film was found to contain C and it is suggested that C passivates the H donors or acts as an acceptor, producing compensated material in this case. Therefore, it is concluded that the unintentional impurities play an important role for the unintentional n-type conductivity in InN. We suggest a scenario of H incorporation in InN that may reconcile the previously reported observations for the different role of impurities and dislocations for the unintentional n-type conductivity in InN.

Darakchieva, Vanya, et al. (författare)
Role of impurities and dislocations for the unintentional n-type conductivity in InN
2009
Ingår i: PHYSICA B-CONDENSED MATTER. - : Elsevier BV. - 0921-4526. ; 404:22, s. 4476-4481
Tidskriftsartikel (refereegranskat)abstract
- We present a study on the role of dislocations and impurities for the unintentional n-type conductivity in high-quality InN grown by molecular beam epitaxy. The dislocation densities and H profiles in films with free electron concentrations in the low 10(17) cm(-1) and mid 10(18) cm(-3) range are measured, and analyzed in a comparative manner. It is shown that dislocations alone could not account for the free electron behavior in the InN films. On the other hand, large concentrations of H sufficient to explain, but exceeding substantially, the observed free electron densities are found. Furthermore, enhanced concentrations of H are revealed at the film surfaces, resembling the free electron behavior with surface electron accumulation. The low-conductive film was found to contain C and it is suggested that C passivates the H donors or acts as an acceptor, producing compensated material in this case. Therefore, it is concluded that the unintentional impurities play an important role for the unintentional n-type conductivity in InN. We suggest a scenario of H incorporation in InN that may reconcile the previously reported observations for the different role of impurities and dislocations for the unintentional n-type conductivity in InN.

Träfflista för sökning "id:"swepub:oai:DiVA.org:liu-52772" "

Avgränsa träffmängd