1.	Bastani, Alireza, et al. (author) Effect of open assembly time and equilibrium moisture content on the penetration of polyurethane adhesive into thermally modified wood 2017 In: The journal of adhesion. - : Taylor & Francis. - 0021-8464 .- 1563-518X .- 1545-5823. ; 93:7, s. 575-583 Journal article (peer-reviewed)abstract The effect of wood moisture content and open assembly time on penetration of polyurethane (PU) adhesive into thermally treated Scots pine (195 and 210°C) was investigated according to effective (EP) and maximum penetration (MP) measurements using fluorescence microscopy. For samples treated at 195°C, a higher EP was noted at 8.6% equilibrium moisture content (EMC) after both assembly times (15 and 30 min) while for samples treated at 210°C, increasing wood moisture content resulted in a significant decrease in EP at 12.5% EMC after 15 min assembly time. Extending open assembly time was found to increase the EP of PU adhesive only in the case of samples treated at 195°C and with 8.6% EMC. For samples treated at both treatment temperatures and after shorter open assembly time, the highest MP observed at moderate EMC levels of 8.6 and 8.2% and the lowest at the higher EMC levels of 13.2 and 12.5%.

Bastani, Alireza, et al. (author)
Effect of open assembly time and equilibrium moisture content on the penetration of polyurethane adhesive into thermally modified wood
2017
In: The journal of adhesion. - : Taylor & Francis. - 0021-8464 .- 1563-518X .- 1545-5823. ; 93:7, s. 575-583
Journal article (peer-reviewed)abstract
- The effect of wood moisture content and open assembly time on penetration of polyurethane (PU) adhesive into thermally treated Scots pine (195 and 210°C) was investigated according to effective (EP) and maximum penetration (MP) measurements using fluorescence microscopy. For samples treated at 195°C, a higher EP was noted at 8.6% equilibrium moisture content (EMC) after both assembly times (15 and 30 min) while for samples treated at 210°C, increasing wood moisture content resulted in a significant decrease in EP at 12.5% EMC after 15 min assembly time. Extending open assembly time was found to increase the EP of PU adhesive only in the case of samples treated at 195°C and with 8.6% EMC. For samples treated at both treatment temperatures and after shorter open assembly time, the highest MP observed at moderate EMC levels of 8.6 and 8.2% and the lowest at the higher EMC levels of 13.2 and 12.5%.