1.	Wang, Ling, et al. (författare) Intensive particle rearrangement in the early stage of spark plasma sintering process 2015 Ingår i: Journal of Asian ceramic societies. - : Informa UK Limited. - 2187-0764. ; 3:2, s. 183-187 Tidskriftsartikel (refereegranskat)abstract The densification behaviors of 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) ceramics during spark plasma sintering (SPS) were analyzed both using the master sintering curve (MSC) approach and by evaluating the temperature dependent evolution of density and densification rate. It was found that densification curves could hardly be fitted using one apparent activation energy value by MSC conception, by which it indicated that more than one densification mechanisms were involved in SPS. Moreover, dependent neither on applied pressure (20-100 MPa) nor heating rates higher than 50 degrees C/min, the maximum densification rate had always been observed at rather similar similar to 78% of theoretical density (TD) accompanied with negligible grain growth. An intensive particle rearrangement mechanism was proposed to dominate the rapid densification to 78% TD in early stage of SPS process, by which it yielded the considerable faster densification rate than those achievable by diffusion-related processes. (C) 2015 The Ceramic Society of Japan and the Korean Ceramic Society.

Wang, Ling, et al. (författare)
Intensive particle rearrangement in the early stage of spark plasma sintering process
2015
Ingår i: Journal of Asian ceramic societies. - : Informa UK Limited. - 2187-0764. ; 3:2, s. 183-187
Tidskriftsartikel (refereegranskat)abstract
- The densification behaviors of 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) ceramics during spark plasma sintering (SPS) were analyzed both using the master sintering curve (MSC) approach and by evaluating the temperature dependent evolution of density and densification rate. It was found that densification curves could hardly be fitted using one apparent activation energy value by MSC conception, by which it indicated that more than one densification mechanisms were involved in SPS. Moreover, dependent neither on applied pressure (20-100 MPa) nor heating rates higher than 50 degrees C/min, the maximum densification rate had always been observed at rather similar similar to 78% of theoretical density (TD) accompanied with negligible grain growth. An intensive particle rearrangement mechanism was proposed to dominate the rapid densification to 78% TD in early stage of SPS process, by which it yielded the considerable faster densification rate than those achievable by diffusion-related processes. (C) 2015 The Ceramic Society of Japan and the Korean Ceramic Society.

Träfflista för sökning "id:"swepub:oai:DiVA.org:su-176205" "