1.	Fallberg, Anna, et al. (författare) CVD of Copper(I) Nitride 2009 Ingår i: Chemical Vapor Deposition. - Weinheim : WILEY-VCH Verlag GmbH & Co. - 0948-1907 .- 1521-3862. ; 15:10-12, s. 300-305 Tidskriftsartikel (refereegranskat)abstract Copper(I) nitride (Cu3N) is deposited by CVD using copper(II) hexafluoroacetylacetonate (Cu(hfaC)(2)), ammonia, and water as precursors. The influences of process parameters on growth rate, phase content, chemical composition and morphology are studied. The introduction of water is found to increase film growth rate on the SiO2 substrate. Films are deposited in the temperature range 250-550 degrees C. Single-phase Cu3N is obtained up to 400 degrees C. A phase mixture Of Cu3N and Cu is obtained at 425 degrees C, while a temperature of 550 degrees C and above yields single-phase Cu. X-ray diffraction (XRD) confirms that Cu3N has the cubic, anti-ReO3-type structure; with a cell parameter in the range 3.805-3.816 angstrom. X-ray photoelectron spectroscopy (XPS) verifies the Cu3N stoichiometry. The films are free from impurities (below the detection limit of 1%) at a large excess of ammonia. Scanning electron microscopy (SEM) shows facetted grains, with the faces becoming more well-defined at higher temperatures.

Fallberg, Anna, et al. (författare)
CVD of Copper(I) Nitride
2009
Ingår i: Chemical Vapor Deposition. - Weinheim : WILEY-VCH Verlag GmbH & Co. - 0948-1907 .- 1521-3862. ; 15:10-12, s. 300-305
Tidskriftsartikel (refereegranskat)abstract
- Copper(I) nitride (Cu3N) is deposited by CVD using copper(II) hexafluoroacetylacetonate (Cu(hfaC)(2)), ammonia, and water as precursors. The influences of process parameters on growth rate, phase content, chemical composition and morphology are studied. The introduction of water is found to increase film growth rate on the SiO2 substrate. Films are deposited in the temperature range 250-550 degrees C. Single-phase Cu3N is obtained up to 400 degrees C. A phase mixture Of Cu3N and Cu is obtained at 425 degrees C, while a temperature of 550 degrees C and above yields single-phase Cu. X-ray diffraction (XRD) confirms that Cu3N has the cubic, anti-ReO3-type structure; with a cell parameter in the range 3.805-3.816 angstrom. X-ray photoelectron spectroscopy (XPS) verifies the Cu3N stoichiometry. The films are free from impurities (below the detection limit of 1%) at a large excess of ammonia. Scanning electron microscopy (SEM) shows facetted grains, with the faces becoming more well-defined at higher temperatures.

Träfflista för sökning "id:"swepub:oai:DiVA.org:uu-110523" "