SwePub - sökning: id:"swepub:oai:DiVA.org:uu-406...

Numrering	Referens	Omslagsbild	Hitta
1.	Tang, Hu, et al. (författare) Boron-Rich Molybdenum Boride with Unusual Short-Range Vacancy Ordering, Anisotropic Hardness, and Superconductivity 2020 Ingår i: Chemistry of Materials. - : AMER CHEMICAL SOC. - 0897-4756 .- 1520-5002. ; 32:1, s. 459-467 Tidskriftsartikel (refereegranskat)abstract Determination of the structures of materials involving more light elements such as boron-rich compounds is challenging and technically important in understanding their varied compositions and superior functionalities. Here we resolve the long-standing uncertainties in structure and composition about the highest boride (termed MoB4, Mo1-xB3, or MoB3) through the rapid formation of large sized boron-rich molybdenum boride under pressure. Using high-quality single-crystal X-ray diffraction analysis and aberration-corrected scanning transmission electron microscopy, we reveal that boron-rich molybdenum boride with a composition of Mo0.757B3 exhibits P6(3)/mmc symmetry with a partial occupancy of 0.514 in 211 Mo sites (Mol), and direct observations reveal the short-range ordering of cation vacancies in (010) crystal planes. Large anisotropic Young's moduli and Vickers hardness are seen for Mo0.757B3, which may be attributed by its two-dimensional boron distributions. Mo0.757B3 is also found to be superconducting with a transition temperature (T-c) of 2.4 K, which was confirmed by measurements of resistivity and magnetic susceptibility. Theoretical calculations suggest that the partial occupancy of Mo atoms plays a crucial role in the emergence of superconductivity.

Tang, Hu, et al. (författare)
Boron-Rich Molybdenum Boride with Unusual Short-Range Vacancy Ordering, Anisotropic Hardness, and Superconductivity
2020
Ingår i: Chemistry of Materials. - : AMER CHEMICAL SOC. - 0897-4756 .- 1520-5002. ; 32:1, s. 459-467
Tidskriftsartikel (refereegranskat)abstract
- Determination of the structures of materials involving more light elements such as boron-rich compounds is challenging and technically important in understanding their varied compositions and superior functionalities. Here we resolve the long-standing uncertainties in structure and composition about the highest boride (termed MoB4, Mo1-xB3, or MoB3) through the rapid formation of large sized boron-rich molybdenum boride under pressure. Using high-quality single-crystal X-ray diffraction analysis and aberration-corrected scanning transmission electron microscopy, we reveal that boron-rich molybdenum boride with a composition of Mo0.757B3 exhibits P6(3)/mmc symmetry with a partial occupancy of 0.514 in 211 Mo sites (Mol), and direct observations reveal the short-range ordering of cation vacancies in (010) crystal planes. Large anisotropic Young's moduli and Vickers hardness are seen for Mo0.757B3, which may be attributed by its two-dimensional boron distributions. Mo0.757B3 is also found to be superconducting with a transition temperature (T-c) of 2.4 K, which was confirmed by measurements of resistivity and magnetic susceptibility. Theoretical calculations suggest that the partial occupancy of Mo atoms plays a crucial role in the emergence of superconductivity.

Träfflista för sökning "id:"swepub:oai:DiVA.org:uu-406060" "

Avgränsa träffmängd