1.	Chen, Ruei-San, et al. (författare) Electronic transport properties in aluminum indium nitride nanorods grown by magnetron sputter epitaxy 2013 Ingår i: Applied Surface Science. - : Elsevier. - 0169-4332 .- 1873-5584. ; 285, s. 625-628 Tidskriftsartikel (refereegranskat)abstract The electronic transport properties of the wide-bandgap aluminum indium nitride (AlInN) nanorods (NRs) grown by ultrahigh-vacuum magnetron sputter epitaxy (MSE) have been studied. The conductivities of the ternary compound nanostructure locates at the value of 15 Q-1 cm -1, which is respectively one and two orders of magnitude lower than the binary GaN and InN counterparts grown by chemical vapor deposition (CVD). The very shallow donor level/band with the activation energy at 11 + 2 meV was obtained by the temperature-dependent measurement. In addition, the photoconductivity has also been investigated. The photoconductive (PC) gain of the NRs device can reach near 2400 under a low bias at 0.1 V and the light intensity at 100W m-2 for ultraviolet response in vacuum. The power-insensitive gain and ambience-dependent photocurrent are also observed, which is attributed to the probable surfacecontrolled PC mechanism in this ternary nitride nanostructure.

Chen, Ruei-San, et al. (författare)
Electronic transport properties in aluminum indium nitride nanorods grown by magnetron sputter epitaxy
2013
Ingår i: Applied Surface Science. - : Elsevier. - 0169-4332 .- 1873-5584. ; 285, s. 625-628
Tidskriftsartikel (refereegranskat)abstract
- The electronic transport properties of the wide-bandgap aluminum indium nitride (AlInN) nanorods (NRs) grown by ultrahigh-vacuum magnetron sputter epitaxy (MSE) have been studied. The conductivities of the ternary compound nanostructure locates at the value of 15 Q-1 cm -1, which is respectively one and two orders of magnitude lower than the binary GaN and InN counterparts grown by chemical vapor deposition (CVD). The very shallow donor level/band with the activation energy at 11 + 2 meV was obtained by the temperature-dependent measurement. In addition, the photoconductivity has also been investigated. The photoconductive (PC) gain of the NRs device can reach near 2400 under a low bias at 0.1 V and the light intensity at 100W m-2 for ultraviolet response in vacuum. The power-insensitive gain and ambience-dependent photocurrent are also observed, which is attributed to the probable surfacecontrolled PC mechanism in this ternary nitride nanostructure.

Träfflista för sökning "onr:"swepub:oai:DiVA.org:liu-98047" "