1.	Yang, Xia, et al. (författare) Effect of Hydrophobic Comonomer Content on Assembling of Poly (N-isopropylacrylamide) and Thermal Properties 2011 Ingår i: Journal of Applied Polymer Science. - : Wiley. - 0021-8995 .- 1097-4628. ; 120:4, s. 2346-2353 Tidskriftsartikel (refereegranskat)abstract Copolymers of N-isopropylacrylamide and octadecyl acrylate (PNO), of which the content of octadecyl acrylate (ODA) was 1.3% (PNO 1.5), 1.7% (PNO 2.0), and 3.0% (PNO 4.0), were prepared using a free radical reaction. Various assemblies were obtained depending on the concentration of PNOs and the contents of ODA. Hydrophobic interaction between ODA residues is likely to act as crosslinker. PNO 1.5 formed hydrogel at the concentration of 7%. With PNO 2.0, hydrogels were formed when the concentration was 5 and 7%. With PNO 4.0, the opaque gel was obtained when the concentration was 7%. Upon heating across the lower critical solution temperature, the hydrogels shrank but the opaque gel was broken down into a suspension. At 40 degrees C, the release degrees of fluorescein isothiocyanate-dextran were much smaller than those of release at 23 degrees C. The temperature-sensitive release is due to temperature-sensitive swelling ratio.

Yang, Xia, et al. (författare)
Effect of Hydrophobic Comonomer Content on Assembling of Poly (N-isopropylacrylamide) and Thermal Properties
2011
Ingår i: Journal of Applied Polymer Science. - : Wiley. - 0021-8995 .- 1097-4628. ; 120:4, s. 2346-2353
Tidskriftsartikel (refereegranskat)abstract
- Copolymers of N-isopropylacrylamide and octadecyl acrylate (PNO), of which the content of octadecyl acrylate (ODA) was 1.3% (PNO 1.5), 1.7% (PNO 2.0), and 3.0% (PNO 4.0), were prepared using a free radical reaction. Various assemblies were obtained depending on the concentration of PNOs and the contents of ODA. Hydrophobic interaction between ODA residues is likely to act as crosslinker. PNO 1.5 formed hydrogel at the concentration of 7%. With PNO 2.0, hydrogels were formed when the concentration was 5 and 7%. With PNO 4.0, the opaque gel was obtained when the concentration was 7%. Upon heating across the lower critical solution temperature, the hydrogels shrank but the opaque gel was broken down into a suspension. At 40 degrees C, the release degrees of fluorescein isothiocyanate-dextran were much smaller than those of release at 23 degrees C. The temperature-sensitive release is due to temperature-sensitive swelling ratio.