1.	Li, Xiaolong, 1991, et al. (författare) Solid solution softening at room temperature and hardening at elevated temperatures: a case by minor Mn addition in a (HfNbTi) 85 Mo 15 refractory high entropy alloy 2023 Ingår i: Materials Research Express. - 2053-1591. ; 10:11 Tidskriftsartikel (refereegranskat)abstract To address the conflict between room-temperature (RT) ductility and high-temperature (HT) strength in single phase bcc-structured refractory high entropy alloys, here we propose to use minor alloying to achieve solid solution softening at RT and simultaneously, solid solution hardening at HT. Our strategy was manifested by minor Mn additions in a RT brittle (HfNbTi)85Mo15 refractory high entropy alloy, where nominal Mn additions ranging from 2 at. % down to 0.03 at. % were seen to soften the base (HfNbTi)85Mo15 alloy at RT, while to harden the base alloy at the temperature range from 400 to 800 °C. The yield stress in all studied alloys showed a three-stage pattern, characterized by a temperature dependent stage at temperatures below 400 °C, followed by a temperature independent stage at intermediate temperatures ranging from 400 to 800 °C, and finally another temperature dependent stage at temperatures higher than 800 °C. The mechanisms for solid solution softening and solid solution hardening in single phase bcc-structured refractory high entropy alloys were discussed, together with their temperature dependence.

Li, Xiaolong, 1991, et al. (författare)
Solid solution softening at room temperature and hardening at elevated temperatures: a case by minor Mn addition in a (HfNbTi) 85 Mo 15 refractory high entropy alloy
2023
Ingår i: Materials Research Express. - 2053-1591. ; 10:11
Tidskriftsartikel (refereegranskat)abstract
- To address the conflict between room-temperature (RT) ductility and high-temperature (HT) strength in single phase bcc-structured refractory high entropy alloys, here we propose to use minor alloying to achieve solid solution softening at RT and simultaneously, solid solution hardening at HT. Our strategy was manifested by minor Mn additions in a RT brittle (HfNbTi)85Mo15 refractory high entropy alloy, where nominal Mn additions ranging from 2 at. % down to 0.03 at. % were seen to soften the base (HfNbTi)85Mo15 alloy at RT, while to harden the base alloy at the temperature range from 400 to 800 °C. The yield stress in all studied alloys showed a three-stage pattern, characterized by a temperature dependent stage at temperatures below 400 °C, followed by a temperature independent stage at intermediate temperatures ranging from 400 to 800 °C, and finally another temperature dependent stage at temperatures higher than 800 °C. The mechanisms for solid solution softening and solid solution hardening in single phase bcc-structured refractory high entropy alloys were discussed, together with their temperature dependence.

Träfflista för sökning "onr:"swepub:oai:research.chalmers.se:f3805e6b-0134-482e-9b19-cc0267a02578" "