| 11. |
- Gottlob, H. D. B., et al.
(författare)
-
Gentle FUSI NiSi metal gate process for high-k dielectric screening
- 2008
-
Ingår i: Microelectronic Engineering. - : Elsevier BV. - 0167-9317 .- 1873-5568. ; 85:10, s. 2019-2021
-
Tidskriftsartikel (refereegranskat)abstract
- In this paper, a process flow well suited for screening of novel high-k dielectrics is presented. In vacuo silicon capping of the dielectrics excludes process and handling induced influences especially if hygroscopic materials are investigated. A gentle, low thermal budget process is demonstrated to form metal gate electrodes by turning the silicon capping into a fully silicided nickel silicide. This process enables the investigation of rare earth oxide based high-k dielectrics and specifically their intrinsic material properties using metal oxide semiconductor (MOS) capacitors. We demonstrate the formation of nickel monosilicide electrodes which show smooth interfaces to the lanthanum- and gadolinium-based high-k oxide films. The dielectrics have equivalent oxide thicknesses of EOT = 0.95 nm (lanthanum silicate) and EOT = 0.6 nm (epitaxial gadolinium oxide).
|
|
| 12. |
- Hurley, P.K., et al.
(författare)
-
Characterization of Interface Defects
- 2013
-
Ingår i: Nanoscale CMOS (ed. Balestra). - : Wiley. ; , s. 545-573
-
Bokkapitel (övrigt vetenskapligt/konstnärligt)
|
|
| 13. |
- Hurley, P. K., et al.
(författare)
-
Interface defects in HfO2, LaSiOx, and Gd2O3 high-k/metal-gate structures on silicon
- 2008
-
Ingår i: Journal of the Electrochemical Society. - : The Electrochemical Society. - 0013-4651 .- 1945-7111. ; 155:2, s. G13-G20
-
Tidskriftsartikel (refereegranskat)abstract
- In this work, we present experimental results examining the energy distribution of the relatively high (> 1 X 10(11) cm(-2)) electrically active interface defects which are commonly observed in high-dielectric-constant (high-k) metal-insulator-silicon systems during high-k process development. This paper extends previous studies on the Si(100)/SiOx/HfO2 system to include a comparative analysis of the density and energy distribution of interface defects for HfO2, lanthanum silicate (LaSiOx), and Gd2O3 thin films on (100) orientation silicon formed by a range of deposition techniques. The analysis of the interface defect density across the energy gap, for samples which experience no H-2/N-2 annealing following the gate stack formation, reveals a peak density (similar to 2 X 10(12) cm(-2) eV(-1) to similar to 1 X 10(13) cm(-2) eV(-1)) at 0.83-0.92 eV above the silicon valence bandedge for the HfO2, LaSiOx, and Gd2O3 thin films on Si (100). The characteristic peak in the interface state density (0.83-0.92 eV) is obtained for samples where no interface silicon oxide layer is observed from transmission electron microscopy. Analysis suggests silicon dangling bond (P-bo) centers as the common origin for the dominant interface defects for the various Si(100)/SiOx/high-k/metal gate systems. The results of forming gas (H-2/N-2) annealing over the temperature range 350-555 degrees C are presented and indicate interface state density reduction, as expected for silicon dangling bond centers. The technological relevance of the results is discussed. (c) 2007 The Electrochemical Society.
|
|
| 14. |
|
|
| 15. |
- Hurley, P.K., et al.
(författare)
-
Interface Defects in HfO2, LaSiOx, and Gd2O3 High-k/MetalGate Structures on Silicon
- 2008
-
Ingår i: J. Electrochem. Soc.. ; 155:2, s. G13-G20
-
Tidskriftsartikel (refereegranskat)abstract
- In this work, we present experimental results examining the energy distribution of the relatively high (>1×10^11 cm−2) electrically active interface defects which are commonly observed in high-dielectric-constant (high-k) metal–insulator–silicon systems during high-k process development. This paper extends previous studies on the Si(100)/SiOx/HfO2 system to include a comparative analysis of the density and energy distribution of interface defects for HfO2, lanthanum silicate (LaSiOx), and Gd2O3 thin films on (100) orientation silicon formed by a range of deposition techniques. The analysis of the interface defect density across the energy gap, for samples which experience no H2/N2 annealing following the gate stack formation, reveals a peak density (~2×10^12 cm−2 eV−1 to ~1×10^13 cm−2 eV−1) at 0.83–0.92 eV above the silicon valence bandedge for the HfO2, LaSiOx, and Gd2O3 thin films on Si(100). The characteristic peak in the interface state density (0.83–0.92 eV) is obtained for samples where no interface silicon oxide layer is observed from transmission electron microscopy. Analysis suggests silicon dangling bond (Pbo) centers as the common origin for the dominant interface defects for the various Si(100)/SiOx/high-k/metal gate systems. The results of forming gas (H2/N2) annealing over the temperature range 350–555°C are presented and indicate interface state density reduction, as expected for silicon dangling bond centers. The technological relevance of the results is discussed.
|
|
| 16. |
|
|
| 17. |
- Lu, Y., et al.
(författare)
-
Leakage current effects on C-V plots of high-k metal-oxide-semiconductor capacitors
- 2009
-
Ingår i: Journal of Vacuum Science & Technology B. - : American Vacuum Society. - 1071-1023 .- 1520-8567 .- 2166-2754 .- 2166-2746. ; 27:1, s. 352-355
-
Tidskriftsartikel (refereegranskat)abstract
- With the employment of ultrathin, high dielectric constant gate materials in advanced semiconductor technology, the conventional capacitance-voltage measurement technique exhibits a series of anomalies. In particular, a nonsaturating increase in the accumulation capacitance with reducing measurement frequency is frequently observed, which has not been adequately explained to our knowledge. In this article, the authors provide an explanation for this anomaly and hence set a criterion for the lower bound on measurement frequency. We then present a model which allows the easy extraction of the required parameters and apply it to an experimental set of data.
|
|
| 18. |
|
|
| 19. |
|
|
| 20. |
- Raeissi, Bahman, 1979, et al.
(författare)
-
High-k-oxide/silicon interfaces characterized by capacitance frequency spectroscopy
- 2007
-
Ingår i: ESSDERC 2007. - 9781424411238 ; , s. 283-286
-
Konferensbidrag (refereegranskat)abstract
- Electron capture into insulator/silicon interface states is investigated for high-k dielectrics of Gd(2)O(3) prepared by MBE and ALD, and for HfO(2) prepared by reactive sputtering, by measuring the frequency dependence of MOS capacitance. The capture cross sections are found to be thermally activated and to increase steeply with the energy depth of the interface electron states. The methodology adopted is considered useful for increasing the understanding of high-k-oxide/silicon interfaces.
|
|