| 1. |
- Barkarmo, Sargon, et al.
(författare)
-
Enhanced bone healing around nanohydroxyapatite-coated polyetheretherketone implants : An experimental study in rabbit bone
- 2014
-
Ingår i: Journal of biomaterials applications. - : Sage Publications. - 0885-3282 .- 1530-8022. ; 29:5, s. 737-747
-
Tidskriftsartikel (refereegranskat)abstract
- Objective: To investigate the bone response to threaded polyetheretherketone (PEEK) implants coated with nanohydroxyapatite. Materials and methods: A total of 39 PEEK implants were coated with nanocrystalline hydroxyapatite and 39 uncoated implants were used as controls. The implant surface was characterized by optical interferometry and scanning electron microscope. The implants were inserted in the tibia and femur of 13 rabbits. After 6 weeks of healing, quantitative and qualitative analyses were performed. Results: The test implants showed significantly higher removal torque test values compared with the control group. Histomorphometric evaluation demonstrated higher bone-to-implant contact for the test implants; however, there were no differences in bone area between the groups. Qualitative histological analyses demonstrated inflammatory cellular reactions in close vicinity of both implant surfaces. A two-cell layer of foreign body giant cells was observed irrespective of sample type. Conclusion: Our findings demonstrate that implants with a threaded design render good stability to PEEK in both coated and uncoated implants. Nanohydroxyapatite-coated PEEK implants demonstrated improved bone formation compared with uncoated controls.
|
|
| 2. |
- Barkarmo, Sargon, et al.
(författare)
-
Nano-hydroxyapatite-coated PEEK implants : a pilot study in rabbit bone
- 2013
-
Ingår i: Journal of Biomedical Materials Research. Part A. - : John Wiley & Sons. - 1549-3296 .- 1552-4965. ; 101A:2, s. 465-471
-
Tidskriftsartikel (refereegranskat)abstract
- Osseointegration of surface-modified polyetheretherketone (PEEK) implants was studied in vivo. A total of 18 cylinder-shaped PEEK implants were inserted in the femurs of nine New Zealand rabbits; half were coated with nanocrystalline hydroxyapatite (nanoHA) and half were uncoated controls. Healing time was 6 weeks. Samples were retrieved with the implant and surrounding tissue, processed to cut and ground sections, and analyzed histomorphometrically. The implant surfaces were analyzed with optical interferometry, scanning electron microscopy (SEM), atomic force microscopy, and X-ray photoelectron spectroscopy (XPS). NanoHA-coated PEEK surfaces had lower height deviation (Sa) than controls [mean ± SD: 0.41 μm (± 0.14) vs. 0.96 μm (± 0.28)]. SEM images showed the nanoHA crystals as a thin layer on the polymer surface. XPS analysis of the coated implants showed a Ca/P ratio of 1.67. Histomorphometry indicated that the nanoHA-coated implants had more bone-to-implant contact [16% (± 4.7) vs. 13% (± 9.3)] and more bone area [52% (± 9.5) vs. 45% (± 11.9)]. We found no difference between smooth nanoHA-coated cylinder-shaped PEEK implants and uncoated controls. However, higher mean bone-to-implant contact indicated better osseointegration in the coated implants than in the uncoated controls. The large number of lost implants was interpreted as a lack of primary stability due to implant design.
|
|
| 3. |
- Gottlow, Jan, 1951, et al.
(författare)
-
An experimental comparison of two different clinically used implant designs and surfaces.
- 2012
-
Ingår i: Clinical implant dentistry and related research. - : Wiley. - 1708-8208 .- 1523-0899. ; 14 Suppl 1
-
Tidskriftsartikel (refereegranskat)abstract
- Various designs of dental implants representing different geometries and surface technologies are commercially available and clinically used in patients. However, data with regard to bone tissue responses and stability for comparison of their biologic performances are rare.
|
|