| 1. |
- Pappas, S. D., et al.
(författare)
-
A Cost-Effective Growth of SiOx Thin Films by Reactive Sputtering : Photoluminescence Tuning
- 2011
-
Ingår i: Journal of Nanoscience and Nanotechnology. - : American Scientific Publishers. - 1533-4880 .- 1533-4899. ; 11:4, s. 3684-3687
-
Tidskriftsartikel (refereegranskat)abstract
- We present a new cost-effective method to produce substoichiometric SiO2 thin films by means of a simple sputter-coater operated at a base pressure of 1 x 10(-3) mbar. During sputtering air is introduced through a fine valve so that the sputtering gas is a mixture of air/Ar. High-resolution electron microscopy shows the formation of amorphous SiOx thin films for the as-deposited samples. The index x approaches 1 when the ratio of the partial pressure of air/Ar tends to 0.1. On the other hand, pure silica is formed when the ratio of the partial pressure of air/Ar approaches 0.5. The films in the as-deposited state show intense green yellow photoluminescence. This fades away with short annealing under air at 950 degrees C. If on the other hand, prolonged annealing is performed under Argon atmosphere at 1000 degrees C, red-infrared photoluminescence is recorded due to the formation of Si nanocrystals embedded in SiO2. This simple method could be suitable for the production of thin SiOx films with embedded nanocrystals for optoelectronic or photovoltaic applications.
|
|
| 2. |
- Poulopoulos, P., et al.
(författare)
-
Growth and Magnetism of Natural Multilayers
- 2011
-
Ingår i: Journal of Nano Research. - 1662-5250. ; 15, s. 95-103
-
Tidskriftsartikel (refereegranskat)abstract
- In this work, we present a simple method to fabricate high quality Ni/NiO multilayers with the use of a single magnetron sputtering head. Namely, at the end of the deposition of each single Ni layer, air is let to flow into the vacuum chamber through a leak valve. Then, a very thin NiO layer (similar to 1nm) is formed by natural oxidation. The process is reproducible and the result is the formation of a multilayer with excellent layering. Magnetization hysteresis loops recorded at 5 K and room temperature reveal a tendency for perpendicular magnetic anisotropy as the thickness of the individual Ni layers decreases. It is shown that the Ni/NiO interface has sizeable positive surface/interface anisotropy, i.e. it favors the development of perpendicular magnetic anisotropy. This is rather unusual for a Ni-based multilayered system and may render Ni/NiO multilayers useful for magneto-optical recording applications.
|
|