1.
Goel, Sneha, 1993-, et al.
(author)
Effect of post-treatments under hot isostatic pressure on microstructural characteristics of EBM-built Alloy 718
2019
In: Additive Manufacturing. - : Elsevier BV. - 2214-8604 .- 2214-7810. ; 28, s. 727-737
Journal article (peer-reviewed) abstract
Electron beam melting (EBM) has emerged as an important additive manufacturing technique. In this study, Alloy 718 produced by EBM was investigated in as-built and post-treated conditions for microstructural characteristics and hardness. The post-treatments investigated were hot isostatic pressing (HIP) and combined HIP + heat treatment (HIP + HT) carried out as a single cycle inside the HIP vessel. Both the post-treatments resulted in significant decrease in defects inevitably present in the as-built material. The columnar grain structure of the as-built material was found to be maintained after post-treatment, with some sporadic localized grain coarsening noted. Although HIP led to complete dissolution of δ and γ′′ phase, stable NbC and TiN (occasionally present) particles were observed in the post-treated specimens. Significant precipitation of γ′′ phase was observed after HIP + HT, which was attributed to the two-step aging heat treatment carried out during HIP + HT. The presence of γ′′ phase or otherwise was correlated to the hardness of the material. While the HIP treatment resulted in drop in hardness, HIP + HT led to ‘recovery’ of the hardness to values exceeding those exhibited by the as-built material.
2.
Goel, Sneha, 1993-, et al.
(author)
The Effect of Location and Post-treatment on the Microstructure of EBM-Built Alloy 718
2018
In: Proceedings of the 9th International Symposium on Superalloy 718 & Derivatives. - Cham : Springer. - 2367-1696 .- 2367-1181. - 9783319894799 - 9783319894805 ; , s. 115-129
Conference paper (peer-reviewed) abstract
Additive manufacturing (AM) of Ni-based superalloys such as Alloy 718 may obviate the need for difficult machining and welding operations associated with geometrically intricate parts, thus potentially expanding design possibilities and facilitating cost-effective manufacture of complex components. However, processing AM builds completely free from defects, which may impair mechanical properties such as fatigue and ductility, is challenging. Anisotropic properties, microstructural heterogeneities and local formation of undesired phases are additional concerns that have motivated post-treatment of AM builds. This work investigates the microstructural changes associated with post-treatment of Alloy 718 specimens produced by Electron Beam Melting (EBM) for as-built microstructures at 3 build heights: near base plate, in the middle of build and near the top of the build. Two different post-treatment conditions, hot isostatic pressing (HIP) alone and a combined HIP with solutionising and two-step aging were examined and compared to the results for the as-built condition. The influence of various post-treatments on minor phase distributions (δ, γ″, carbides), overall porosity, longitudinal grain widths and Vickers microhardness was considered. The HIP treatment led to significant reduction in overall porosity and dissolution of δ phase, which led to appreciable grain growth for both post-treatment conditions. The variation in hardness noted as a function of build height for the as-built specimens was eliminated after post-treatment. Overall, the hardness was found to decrease after HIP and increase after the full HIP, solutionising and aging treatment, which was attributed to dissolution of γ″ during HIP and its re-precipitation in subsequent heat treatment steps.
3.
Kumara, Chamara, et al.
(author)
Microstructure modelling of laser metal powder directed energy deposition of alloy 718
2019
In: Additive Manufacturing. - : Elsevier. - 2214-8604 .- 2214-7810. ; 25, s. 357-364
Journal article (peer-reviewed) abstract
A multi-component and multi-phase-field modelling approach, combined with transformation kinetics modelling, was used to model microstructure evolution during laser metal powder directed energy deposition of Alloy 718 and subsequent heat treatments. Experimental temperature measurements were utilised to predict microstructural evolution during successive addition of layers. Segregation of alloying elements as well as formation of Laves and δ phase was specifically modelled. The predicted elemental concentrations were then used in transformation kinetics to estimate changes in Continuous Cooling Transformation (CCT) and Time Temperature Transformation (TTT) diagrams for Alloy 718. Modelling results showed good agreement with experimentally observed phase evolution within the microstructure. The results indicate that the approach can be a valuable tool, both for improving process understanding and for process development including subsequent heat treatment.
4.
Puneet, C., et al.
(author)
CrAlSiN nanocomposite thin films for high-speed machining applications
2018
In: Materials and Manufacturing Processes. - : Informa UK Limited. - 1042-6914 .- 1532-2475. ; 33:4, s. 371-377
Journal article (peer-reviewed) abstract
CrAlSiN nanocomposite thin films with varying film chemistry were developed on tungsten carbide (WC)specimens using cylindrical cathodic arc physical vapor deposition (c-CAPVD) technique. The physical, mechanical, and tribological properties of all the films were comprehensively investigated for arriving at the film chemistry leading to the best properties with respect to mechanical applications. The best tribo-mechanical properties were obtained in films with Cr/(AlþSi) ratio of 1.2. This coating with best properties was translated on to WC drill bits for machining tests. The Al and Si content has shown major influence on the adhesion strength and phase constitution of the films, with a considerable change in residual stress too. The superior properties achieved could be attributed to the formation of an ear-perfect nanocomposite structure, with the crystalline CrAlN phase surrounded by an amorphous Si3N4 phase. The tool life of the coated CrAlSiN tools was investigated during dry machining of EN 24material. In comparison to the tool life of an uncoated tool and a TiAlSiN-coated tool, the best CrAlSiN coatings synthesized in this study performed exceedingly well. The present study clearly demonstrates the advantages of CrAlSiN over other existing similar coatings for high-speed machining.
5.
Ganvir, Ashish, 1991-, et al.
(author)
A Facile Approach to Deposit Graphenaceous Composite Coatings by Suspension Plasma Spraying
2019
In: Coatings. - : MDPI AG. - 2079-6412. ; 9:3
Journal article (peer-reviewed) abstract
This paper demonstrates, for the first time ever, the deposition of graphenaceous composite coatings using an easy, yet robust, suspension plasma spraying (SPS) process. As a case study, a composite coating comprising 8 wt.% of yttria-stabilized-zirconia (8YSZ) and reinforced with graphene oxide (GO) was deposited on a steel substrate. The coatings were sprayed using an 8YSZ-GO mixed suspension with varied plasma spray parameters. Establishing the possibility of retaining the graphene in a ceramic matrix using SPS was of specific interest. Electron microscopy and Raman spectroscopy confirmed the presence of graphenaceous material distributed throughout the coating in the 8YSZ matrix. The experimental results discussed in this work confirm that SPS is an immensely attractive pathway to incorporate a graphenaceous material into virtually any matrix material and can potentially have major implications in enabling the deposition of large-area graphene-containing coatings for diverse functional applications.
6.
Goel, Sneha, 1993-, et al.
(author)
Axial suspension plasma spraying of Al2O3 coatings for superior tribological properties
2017
In: Surface & Coatings Technology. - : ELSEVIER SCIENCE SA. - 0257-8972 .- 1879-3347. ; 315, s. 80-87
Journal article (peer-reviewed) abstract
Suspension plasma spray is a relatively new thermal spray technique which enables feeding of fine powder to produce advanced coatings for varied applications. This work investigates the difference in structure and performance of Al2O3 coatings manufactured using conventional micron-sized powder feedstock and a suspension of sub-micron to few micron sized powder. Axial injection was implemented for deposition in both cases. The effect of feedstock size and processing on the tribological performance of the two coatings was of specific interest. The coatings were characterized by Optical and Scanning Electron Microscopy, micro-hardness and scratch resistance testing, and their dry sliding wear performance evaluated. The suspension sprayed coatings yielded significantly higher scratch resistance, lower friction coefficient and reduced wear rate compared to conventional coatings. The improved tribological behaviour of the former is attributable to finer porosity, smaller splat sizes, and improved interlamellar bonding.
7.
Zhang, Pimin, 1990-, et al.
(author)
Effects of surface finish on the initial oxidation of HVAF-sprayed NiCoCrAlY coatings
2019
In: Surface & Coatings Technology. - Elsevier : Elsevier BV. - 0257-8972 .- 1879-3347. ; 364, s. 43-56
Journal article (peer-reviewed) abstract
Oxide scale formed on HVAF-sprayed NiCoCrAlY coatings and the effect of surface treatment were investigated by a multi-approach study combining photo-stimulated luminescence, microstructural observation and mass gain. The initial oxidationbehaviour of as-sprayed, polished and shot-peened coatings at 1000 °C is studied. Both polished and shot-peened coatings exhibited superior performance due to rapid formation of α-Al2O3 fully covering the coating and suppressing the growth of transient alumina, assisted by a high density of α-Al2O3 nuclei on surface treatment induced defects. Moreover, the fast development of a two-layer alumina scale consisting of an inward-grown inner α-Al2O3 layer and an outer layer transformed from outward-grown transient alumina resulted in a higher oxide growth rate of the as-sprayed coating.
8.
9.
Jafari, Reza, et al.
(author)
KCl-Induced High Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air
2018
In: Journal of thermal spray technology (Print). - : Springer Science and Business Media LLC. - 1059-9630 .- 1544-1016. ; 27:3, s. 500-511
Journal article (peer-reviewed) abstract
KCl-induced high temperature corrosion behavior of four HVAF-sprayed Ni-based coatings (Ni21Cr, Ni5Al, Ni21Cr7Al1Y, and Ni21Cr9Mo) under KCl deposit has been investigated in ambient air at 600°C up to 168h. The coatings were deposited onto 16Mo3 steel - a widely used boiler tube material.Uncoated substrate, 304L and Sanicro25 were used as reference materials in the test environment.SEM/EDS and XRD techniques were utilized to characterize the as-sprayed and exposed samples.The results showed that the small addition of KCl significantly accelerated degradation to the coatings. All coatings provided better corrosion resistance compared to the reference materials. The alumina-forming Ni5Al coating under KCl deposit was capable of forming a more protective oxide scale compared to the chromia-forming coatings as penetration of Cl through diffusion paths was hindered. Both active corrosion and chromate formation mechanisms were found to be responsible for Page 1 of 23ASM the corrosion damages. The corrosion resistance of the coatings based on the microstructure analysis and kinetics had the following ranking (from the best to worst): Ni5Al >Ni21Cr> Ni21Cr7Al1Y>Ni21Cr9Mo.
10.
Sadeghimeresht, Esmaeil, 1985-, et al.
(author)
Chlorine-induced high temperature corrosion of HVAF-sprayed Ni-based alumina and chromia forming coatings
2018
In: Corrosion Science. - : Elsevier BV. - 0010-938X .- 1879-0496. ; 132:March, s. 170-184
Journal article (peer-reviewed) abstract
Chlorine-induced corrosion of HVAF-sprayed Ni21Cr and Ni5Al coatings was investigated in 5 vol.% O2 + 500vppm HCl + N2 with and without KCl at 600 °C up to 168 h. Both coatings were protective in the absence of KCl. With KCl, Ni21Cr degraded through a two-stage mechanism: 1) formation of K2CrO4 followed by diffusion of Cl− through the oxide grain boundaries to yield chlorine and a non-protective oxide, and 2) inward diffusion of chlorine though defects in the non-protective oxide, leading to breakaway oxidation. Cl−/Cl2 could not diffuse through the protective alumina scale formed on Ni5Al, hence the corrosion resistance increased.