Towards understanding micro-galvanic activities in localised corrosion of AA2099 aluminium alloy

• The micro-galvanic interactions between Cu-Fe-Mn-Li-containing aluminides and the alloy matrix of aluminium alloy AA2099 during chloride-induced corrosion were investigated in-situ with real-time monitoring of the local contact potential difference (VCPD) using the scanning Kelvin probe force microscopy (SKPFM) at controlled relative humidities. The aluminides showed noble potentials and were able to ennoble their neighbouring matrix sites when a cluster of aluminides surrounded the matrix. The matrix, hence, adopted a more positive VCPD, towards that of the aluminides. The anode-to-cathode ratio changed throughout the corrosion exposure and was seen to show a dynamic character. Much higher local VCPD activities were recorded during the earliest stages of corrosion, when the Al-Li AA2099 surface was first exposed to high humidities, than in later RH cycles; a phenomenon not seen in other aluminium alloys.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

AA2099

Atmospheric corrosion

Localised corrosion

Relative humidity

SKPFM

Aluminum alloys

Aluminum corrosion

Atmospheric humidity

Binary alloys

Chlorine compounds

Copper alloys

Copper corrosion

Electrodes

Galvanic corrosion

Iron alloys

Lithium alloys

Metallic matrix composites

Alloy matrix

Aluminides

Chloride induced corrosion

Galvanic interaction

Li$++$

Localized corrosion

matrix

Real time monitoring

Scanning Kelvin probe force microscopy

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)