Low Temperature Synthesis of Stable γ-CsPbI 3 Perovskite Layers for Solar Cells Obtained by High Throughput Experimentation

• The structural phases and optoelectronic properties of coevaporated CsPbI 3 thin films with a wide range of [CsI]/[PbI 2 ] compositional ratios are investigated using high throughput experimentation and gradient samples. It is found that for CsI-rich growth conditions, CsPbI 3 can be synthesized directly at low temperature into the distorted perovskite γ-CsPbI 3 phase without detectable secondary phases. In contrast, PbI 2 -rich growth conditions are found to lead to the non-perovskite δ-phase. Photoluminescence spectroscopy and optical-pump THz-probe mapping show carrier lifetimes larger than 75 ns and charge carrier (sum) mobilities larger than 60 cm 2 V −1 s −1 for the γ-phase, indicating their suitability for high efficiency solar cells. The dependence of the carrier mobilities and luminescence peak energy on the Cs-content in the films indicates the presence of Schottky defect pairs, which may cause the stabilization of the γ-phase. Building on these results, p–i–n type solar cells with a maximum efficiency exceeding 12% and high shelf stability of more than 1200 h are demonstrated, which in the future could still be significantly improved, judging on their bulk optoelectronic properties.

Ämnesord

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Nyckelord

coevaporation

high throughput characterization

inorganic halide perovskites

optoelectronics

thin film solar cells

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)