Magnesium solubilit...
Abstract
Ämnesord
Stäng
- Magnesium and silicon concentrations in the interior of primary α-Al of Al-7Si-Mg alloys were studied at temperatures in the liquid-solid range and just after solidification was completed. Analysis of the results showed that the magnesium concentration in the interior of primary α-Al is very low in the temperatures range from the liquidus to the start of the Al-Si eutectic reaction. Formation of silicon-rich phases during eutectic reactions, such as eutectic silicon and β-Al5FeSi, phases trigger a significant increase in the magnesium concentration in the interior of primary α-Al, when sufficient time is allowed for solid-state diffusion to occur. When fast cooling rates are applied during the Al-Si eutectic reaction, most of the magnesium is retained in π-Al8FeMg3Si6 and Mg2Si phases formed during solidification. Semi-solid Al-7Si-Mg castings were produced with varying magnesium contents, and the mechanical properties were evaluated in the as-cast, T5 and T6 conditions. It was found that the 0.2% offset yield strength of the semi-solid Al-7Si-Mg castings in the T5 and T6 conditions increases linearly with the square root of the magnesium concentration in the interior of the α-Al globules formed during the slurry preparation process.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Aluminium alloys
- Heat treatment
- Mechanical properties
- Rheocasting
- Solid-solution
- Solubility