Concluding destructive investigation of a nine-year-old marine-exposed cracked concrete panel

• This study undertaken on a nine-year-old cracked concrete panel further investigates the impact of cracks on the corrosion performance of conventional steel reinforcement in marine-exposed concrete to explain observed monitoring data. The present data covers seven 1.80 m long (12.6 m) reinforcing bars embedded in good quality concrete (w/b = 0.40 and cover >75 mm). Each bar was crossed by two horizontal cracks (surface crack widths 0.20–0.30 mm). The investigation showed no corrosion on the surface of the reinforcing bars, in either cracked or uncracked areas. Two of the seven reinforcing bars were instrumented in the vicinity of the cracks. Extensive corrosion was found in the interior of all instrumented parts of these bars. This may explain the monitoring data despite the lack of corrosion on the exterior surface of the two instrumented rebars. However, with no other weaknesses, the remaining conventional rebars showed no impact from the cracks.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Samhällsbyggnadsteknik -- Infrastrukturteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Civil Engineering -- Infrastructure Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Characterization

Reinforcement corrosion

In-situ marine exposure

Cracks

Reinforced concrete

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)