1. |
- Han, Fenglan, et al.
(författare)
-
Environmental performance of fluorite used to catalyze MgO reduction in pidgeon process
- 2012
-
Ingår i: Advanced Materials Research. - 1022-6680 .- 1662-8985. ; 577, s. 31-38
-
Tidskriftsartikel (refereegranskat)abstract
- Environmental performances of fluorite used as catalyzer for chemical reaction between MgO and Si were investigated by performing pilot scale experiments of Mg production. F amounts of 0.012-0.116 kg were added in the charged briquettes and Mg slag generated from the chemical reaction in most of the tests weighted 4.26-4.96 kg with F contents ranging 0.21-2.52%. Based on high recoveries of F, 83-100%, in the slag after the reaction, it is estimated that there are little or no F compounds leaving the retorts during the pilot tests. However, high amount of F, 72.9 mg/kg, was leached out from an Mg slag sample obtained from an Mg plant, making it necessary to decrease amount of fluorite used as catalyzer for the reaction or to improve operation conditions, thus, enhancing rate for chemical reaction between MgO and Si in Pidgeon process
|
|
2. |
- Han, Fenglan, et al.
(författare)
-
Fluoride evaporation during thermal treatment of waste slag from Mg production using pidgeon process
- 2012
-
Ingår i: Advanced Materials Research. - 1022-6680 .- 1662-8985. ; 581-582, s. 1044-1049
-
Tidskriftsartikel (refereegranskat)abstract
- Fluoride evaporation from Mg slag samples was investigated. F content in the original slag sample from an Mg factory was 1.65%, which decreases to 0.98-1.54% in the samples heated at 1000-1400°C for 3 hours. The values of F evaporation from the test samples were 6.7-40.6%. The fluorides may evaporate in the atmosphere, causing air pollution. Some suggestions were presented based on study results obtained to minimize fluoride emissions and improve environmental performances of the Mg production by using Pidgeon process
|
|
3. |
- Han, Fenglan, et al.
(författare)
-
Treatments of magnesium slag to recycle waste from Pidgeon process
- 2012
-
Ingår i: Advanced Materials Research. - 1022-6680 .- 1662-8985. ; , s. 1657-1667
-
Tidskriftsartikel (refereegranskat)abstract
- Magnesium slag powder from a local magnesium plant was treated to improve the volume stability for its application as building materials. The slag was mixed with borates, pressed into briquettes, and then sintered at high temperature. SEM studies show that at the higher temperature Ca 2SiO4 polymorphs were stabilized by Na and B ions in the added borates. The free MgO content in the slag was also decreased by the sintering treatment. The slag powder, after mixing with 0.4-0.6% of borates and sintered at 1200°C in 5-6 hours, has become volume stable aggregates. It is then possible to use the treated slag in constructions, saving valuable natural resources and decreasing the global warming impact from magnesium production via Pidgeon process
|
|
4. |
- Wu, Laner, et al.
(författare)
-
Fluoride emissions from Pidgeon process for magnesium production
- 2012
-
Konferensbidrag (refereegranskat)abstract
- Primary magnesium is nowadays produced in China via Pidgeon process. An important reaction in the process is silicothermic reduction of MgO from dolime near 1200ºC under pressure of 2-10 Pa to generate Mg vapor. Fluorite, ranging 2-3% (mass fraction), is usually mixed with the raw materials to catalyze the reaction. Under the process conditions, CaF2 in the fluorite may form some fluorides to vaporize, thus polluting air. The fluorides remaining in the solid process waste, the Mg slag, may be dissolved to cause water pollution.In the present study, experiments were performed by using retorts of pilot scale in a maffle furnace to simulate the Pidgeon process for primary Mg production. The test materials, briquettes of 5.6-10 kg made of dolime, ferrosilicon and fluorite, were charged in the retorts and heated under conditions similar to the industry operation. Fluoride minerals in the Mg slag from the simulation experiments were identified by XRD and SEM-EDS techniques. Quantities of some F-containing phases formed in the process under equilibrium condition were calculated by FactSage 6.2 thermodynamic package. Fluoride distributions were determined to establish an F-balance among the input and output materials. Besides, slag samples from a magnesium plant were also characterized, including leaching test according to EN 12457-2.Based on these results, fluoride impacts on the environment were evaluated and discussed. Suggestions were also presented to minimize the environmental impacts from primary Mg production using the Pidgeon process.
|
|