| 1. |
- Forsling, Robin, 1988-, et al.
(författare)
-
Conservative Linear Unbiased Estimation Under Partially Known Covariances
- 2022
-
Ingår i: IEEE Transactions on Signal Processing. - : IEEE. - 1053-587X .- 1941-0476. ; 70, s. 3123-3135
-
Tidskriftsartikel (refereegranskat)abstract
- Mean square error optimal estimation requires the full correlation structure to be available. Unfortunately, it is not always possible to maintain full knowledge about the correlations. One example is decentralized data fusion where the cross-correlations between estimates are unknown, partly due to information sharing. To avoid underestimating the covariance of an estimate in such situations, conservative estimation is one option. In this paper the conservative linear unbiased estimator is formalized including optimality criteria. Fundamental bounds of the optimal conservative linear unbiased estimator are derived. A main contribution is a general approach for computing the proposed estimator based on robust optimization. Furthermore, it is shown that several existing estimation algorithms are special cases of the optimal conservative linear unbiased estimator. An evaluation verifies the theoretical considerations and shows that the optimization based approach performs better than existing conservative estimation methods in certain cases.
|
|
| 2. |
- Balachandramurthi, Arun Ramanathan, 1989-, et al.
(författare)
-
Anisotropic fatigue properties of Alloy 718 manufactured by Electron Beam Powder Bed Fusion
- 2020
-
Ingår i: International Journal of Fatigue. - : Elsevier. - 0142-1123 .- 1879-3452. ; 141
-
Tidskriftsartikel (refereegranskat)abstract
- In this study, Alloy 718 specimens manufactured by Electron Beam Powder Bed Fusion process are subjected to two different post-treatments to have different microstructural features. Low cycle fatigue testing has been performed both parallel and transverse to the build direction. EB-PBF Alloy 718 exhibits anisotropic fatigue behaviour; the fatigue life is better along the parallel direction compared to the transverse direction. The anisotropy in fatigue life is related to the anisotropy in the Young’s modulus. The pseudo-elastic stress vs. fatigue life approach is presented as a potential solution to handle anisotropy in fatigue life assessment of additively manufactured engineering components. © 2020 The Authors
|
|
| 3. |
- Balachandramurthi, Arun Ramanathan, 1989-, et al.
(författare)
-
On the microstructure of laser beam powder bed fusion alloy 718 and its influence on the low cycle fatigue behaviour
- 2020
-
Ingår i: Materials. - : MDPI AG. - 1996-1944 .- 1996-1944. ; 13:22
-
Tidskriftsartikel (refereegranskat)abstract
- Additive manufacturing of Alloy 718 has become a popular subject of research in recent years. Understanding the process-microstructure-property relationship of additively manufactured Alloy 718 is crucial for maturing the technology to manufacture critical components. Fatigue behaviour is a key mechanical property that is required in applications such as gas turbines. Therefore, in the present work, low cycle fatigue behaviour of Alloy 718 manufactured by laser beam powder bed fusion process has been investigated. The material was tested in as-built condition as well as after two different thermal post-treatments. Three orientations with respect to the building direction were tested to evaluate the anisotropy. Testing was performed at room temperature under controlled amplitudes of strain. It was found that defects, inclusions, strengthening precipitates, and Young’s modulus influence the fatigue behaviour under strain-controlled conditions. The strengthening precipitates affected the deformation mechanism as well as the cycle-dependent hardening/softening behaviour. The defects and the inclusions had a detrimental effect on fatigue life. The presence of Laves phase in LB-PBF Alloy 718 did not have a detrimental effect on fatigue life. Young’s modulus was anisotropic and it contributed to the anisotropy in strain-life relationship. Pseudo-elastic stress vs. fatigue life approach could be used to handle the modulus-induced anisotropy in the strain-life relationship. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.
|
|
| 4. |
- Huber, Johannes Albert Josef, 1989-, et al.
(författare)
-
Nondestructive Testing of Timber Prior to Sawing Using Finite Element Models Based on X-ray Computed Tomography Data - A Preliminary Study
- 2022
-
Ingår i: Proceedings: 22nd International Nondestructive Testing and Evaluation of Wood Symposium. - Madison, WI, USA : United States Department of Agriculture. ; , s. 200-200
-
Konferensbidrag (övrigt vetenskapligt/konstnärligt)abstract
- X-ray computed tomography (CT) of wood delivers internal density data of a scanned object, where, depending on the resolution, internal features like the pith, annual rings and knots can be identified. Some sawmills use CT scanners in front of the saw line to determine the optimal positioning of the log in the saw, to maximise the value yield of the sawn products. We envision that the gathered CT data also could be used for mechanical evaluations of the timber using numerical models of boards prior to sawing. In a recent study by the authors, a method was developed to create 3D and 1D finite element (FE) models based on CT scans of dried sawn timber, which could predict bending stiffness and strength in bending simulations with high accuracy. The objective of the present study is to explore how the method can be adapted to CT scans of logs before sawing. Our preliminary study was based on CT data of green Norway Spruce logs and the corresponding scans of dried sawn timber. The stiffness and strength were evaluated using four-point bending tests. Additionally, the resonance frequency of the logs was recorded. The corresponding volume of each piece of sawn timber was extracted from the log data and an FE model was created. The model accounted for the pith, the annual rings, the knots, and the local fibre deviations around knots. Various laws for local stiffness and different failure criteria were tested. The study showed how FE models of virtual pieces of sawn timber can be created from CT data and what obstacles need to be overcome for further development of the presented method. The results indicated that more detailed evaluations of the relationship between local stiffness and density may be required, in specific for knots and for wood in green state.
|
|
| 5. |
- Kjellsson, Henrik, et al.
(författare)
-
High Temperature Fatigue Performance of Electron Beam Powder Bed Fusion Manufactured Alloy 718
- 2022
-
Ingår i: Metallurgical and Materials Transactions. A. - : Springer Nature. - 1073-5623 .- 1543-1940. ; 53, s. 2496-2514
-
Tidskriftsartikel (refereegranskat)abstract
- The microstructure and mechanical properties of additively manufactured (AM) parts have been shown to be different from that of cast and wrought counterparts. In this study, electron beam powder bed fusion (EB-PBF) fabricated Alloy 718 was exposed to three different heat treatment routes followed by strain-controlled fatigue testing at 550 degrees C. The fatigue tests were performed with specimens built with their center axis parallel and transverse relative to the build direction. The microstructure showed saturated precipitation of delta-Ni3Nb after repeated solution treatment at 954 degrees C. In contrast, no delta-Ni3Nb precipitates could be observed after a single-step solution treatment at 1025 degrees C. However, the disparity of secondary phases showed no noticeable influence on the fatigue life. A significant difference in fatigue behavior was noted between the parallel and transverse directions. The specimens loaded parallel to the elongated grains showed on average similar to 5x greater life in comparison to the perpendicularly loaded specimens. Compared to corresponding heat-treated material conditions tested at ambient temperature, the specimens showed lower life at high strain amplitude and superior life at low strain amplitude. Moreover, competitive internal and surface failure modes were observed at the lower strain amplitudes while for the higher strain ranges, surface failure modes dominated. (C) The Author(s) 2022
|
|
| 6. |
- Sadeghi, Esmaeil, 1985-, et al.
(författare)
-
Fatigue crack initiation and propagation in Alloy 718 with a bimodal grain morphology built via electron beam-powder bed fusion
- 2021
-
Ingår i: Materials Science & Engineering. - : Elsevier Ltd. - 0921-5093 .- 1873-4936. ; 827
-
Tidskriftsartikel (refereegranskat)abstract
- A unique melting strategy was implemented in electron beam-powder bed fusion (EB-PBF) of Alloy 718, resulting in the formation of a bimodal grain morphology consisting of fine equiaxed and columnar grains. The microstructure was preserved following various thermal post-treatments. The post-treated specimens were exposed to low cycle fatigue (LCF), and fatigue crack growth (FCG) tests in ambient air at 600 °C under pure and dwell-time (120 s) fatigue cycles. Clustered inclusions spanned a region of 100-600 µm in length acted as the crack initiation site, reducing the specimens' total fatigue life. When compared to pure fatigue cycles, dwell-time fatigue cycles reduced LCF life by approximately 35%, regardless of the thermal post-treatments. Due to a high fraction of grain boundary area in the as-built EB-PBF specimens, oxygen diffusion across the grain boundaries was enhanced. The intergranular fracture mode was favored in the plastic zone ahead of the crack tip, leading to rapid crack growth. No unbroken ligaments behind the crack front were found by high-resolution X-ray computed tomography, which was consistent with a large crack opening displacement linked to severe deformation around the crack tip.
|
|
| 7. |
- Westerlund, Emil, et al.
(författare)
-
Correlation of mitochondrial respiration in platelets, peripheral blood mononuclear cells and muscle fibers
- 2024
-
Ingår i: Heliyon. - 2405-8440. ; 10:5
-
Tidskriftsartikel (refereegranskat)abstract
- There is a growing interest for the possibility of using peripheral blood cells (including platelets) as markers for mitochondrial function in less accessible tissues. Only a few studies have examined the correlation between respiration in blood and muscle tissue, with small sample sizes and conflicting results. This study investigated the correlation of mitochondrial respiration within and across tissues. Additional analyses were performed to elucidate which blood cell type would be most useful for assessing systemic mitochondrial function. There was a significant but weak within tissue correlation between platelets and peripheral blood mononuclear cells (PBMCs). Neither PBMCs nor platelet respiration correlated significantly with muscle respiration. Muscle fibers from a group of athletes had higher mass-specific respiration, due to higher mitochondrial content than non-athlete controls, but this finding was not replicated in either of the blood cell types. In a group of patients with primary mitochondrial diseases, there were significant differences in blood cell respiration compared to healthy controls, particularly in platelets. Platelet respiration generally correlated better with the citrate synthase activity of each sample, in comparison to PBMCs. In conclusion, this study does not support the theory that blood cells can be used as accurate biomarkers to detect minor alterations in muscle respiration. However, in some instances, pronounced mitochondrial abnormalities might be reflected across tissues and detectable in blood cells, with more promising findings for platelets than PBMCs.
|
|