  • Ferroelectric properties of dense nanocrystalline BaTiO3 ceramics
  • 2004
  • Ingår i: Nanotechnology. - : IOP Publishing. - 0957-4484 .- 1361-6528. ; 15:9, s. 1113-1117
  • Tidskriftsartikel (refereegranskat)abstract
    • Dense BaTiO3 ceramics with 50 nm average grain size obtained by spark plasma sintering were investigated. The dielectric data show a broad ferro-para phase transition with a maximum permittivity of approximate to1100 at 390 K and 1 kHz. The local ferroelectric switching behaviour was investigated by piezoresponse force microscopy. Typical piezoelectric hysteresis loops were recorded at different positions of the sample. The present results provide experimental evidence for polarization switching at the local scale, indicating that the critical grain size for the disappearance of ferroelectric behaviour in dense, bulk BaTiO3 nanocrystalline ceramics is below 50 nm.
  •  
2.
  • Mitoseriu, L., et al. (författare)
  • Local switching properties of dense nanocrystalline BaTiO3 ceramics
  • 2004
  • Ingår i: Applied Physics Letters. - : AIP Publishing. - 0003-6951 .- 1077-3118. ; 84:13, s. 2418-2420
  • Tidskriftsartikel (refereegranskat)abstract
    • The switching properties of dense BaTiO3 ceramics with 50 nm average grain size were investigated at local scale by piezoresponse force microscopy. Large areas with low piezoelectrical activity beside islands with strong piezoresponse were found. The application of electric fields induces stable domain structures and changes in the polarization state far away from the probing area, probably via trans-granular dipole interactions. Piezoelectric hysteresis loops were recorded on various positions, even in regions with initial zero piezoresponse, which possibly showed a superparaelectric behavior. The results are incontestable proof that 50 nm BaTiO3 ceramics retain ferroelectricity at a local scale.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-2 av 2
Typ av publikation
tidskriftsartikel (2)
Typ av innehåll
refereegranskat (2)
Författare/redaktör
Zhao, Zhe, 1973- (2)
Nygren, M. (2)
Viviani, M. (2)
Nanni, P (2)
Buscaglia, M. T. (2)
Buscaglia, V. (2)
visa fler...
Mitoseriu, L. (2)
Testino, A. (2)
Harnagea, C. (2)
Savinov, M. (1)
Petzelt, J. (1)
visa färre...
Lärosäte
Kungliga Tekniska Högskolan (2)
Språk
Engelska (2)
Forskningsämne (UKÄ/SCB)
Teknik (2)
År
2004 (2)Ta bort avgränsningen

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy