- Siwale, Workson, et al.
(författare)
-
Influence on off-gassing during storage of Scots pine wood pellets produced from sawdust with different extractive contents
- 2022
-
Ingår i: Biomass and Bioenergy. - : Elsevier. - 0961-9534 .- 1873-2909. ; 156
-
Tidskriftsartikel (refereegranskat)abstract
- Off-gassing and self-heating are the major challenges when it comes to transportation and storage of wood pellets. The heat generated due to self-heating poses a fire risk while off-gassing of toxic gasses such as carbon monoxide (CO) and some volatile organic compounds (VOCs) is an environmental and human health risk. With the increase in production volumes of wood pellets which has subsequently increased the amounts of wood pellets in transportation and storage, there is need to find lasting solutions to off-gassing and self-heating of wood pellets. The objective of this study was to test the off-gassing abilities of Scots pine wood pellets produced from sawdust with varying amounts of extractives. The aim is to come up with raw material pre-treatment measures so as to produce wood pellets that are not liable to off-gassing. Six (6) types of sawdust raw materials namely; fresh pine sawdust (FPS), stored pine sawdust (SPS), sawdust plus pine rosin (PRS), sawdust plus linseed oil (LOS), sawdust plus tall oil (TOS) and acetone extracted sawdust (AES) were used to produce the pellets. The produced pellets were then subjected to off-gassing tests under controlled conditions using the ECOM J2KN analyser. The concentrations of carbon monoxide, carbon dioxide and methane increased with storage time but slowed down towards the end of the nine days test period. The formation of these gasses were largely dependent on the type of extractives present in the raw material and not the total extractive content. The formation of methane started later than the other gases and coincided with the time when residual oxygen was depleted.
|
|
| 3. |
- Siwale, Workson, et al.
(författare)
-
Understanding Off-Gassing of Biofuel Wood Pellets Using Pellets Produced from Pure Microcrystalline Cellulose with Different Additive Oils
- 2022
-
Ingår i: Energies. - : MDPI. - 1996-1073. ; 15:6
-
Tidskriftsartikel (refereegranskat)abstract
- Fuel wood pellets have the tendency of undergoing self-heating and off-gassing during storage and transportation. Self-heating can lead to spontaneous combustion and cause fires while toxic gasses such as carbon monoxide and some volatile organic compounds released due to off-gassing are a human health and environmental hazard. Previous research suggests that the self-heating and off-gassing of wood pellets are as a result of the oxidation of wood extractives. The aim of this study was to identify the extractives, i.e., fatty and resin acids that are responsible for the emissions of carbon monoxide, carbon dioxide and methane from wood pellets by testing the off-gassing tendencies of pellets produced from synthetic microcrystalline cellulose and different additive oils. The additive oils were intentionally selected to represent different types of wood extractives (mainly fatty and resin acids) and they included: tall oil, pine rosin, linseed oil and coconut oil. The highest mean concentrations of carbon monoxide, carbon dioxide and methane were recorded from cellulose pellets with added linseed oil. The concentrations of carbon monoxide and methane for the other four pellet types were negligible and there was no carbon dioxide emission. Pellets with added linseed oil had high off-gas emissions due to the high content of unsaturated fatty acids compared to other pellet types.
|
|
| 4. |
|
|
| 5. |
- White, Jai, 1991-
(författare)
-
From Facets to Flow: The Electrooxidation of Glycerol on Pd-based catalysts
- 2023
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Glycerol, a by-product of biodiesel refineries, has uses in industries such as cosmetics, food, and pharmaceuticals. However, its usage is small compared to the amount of glycerol produced from biodiesel production. Therefore, there is an opportunity to use glycerol, an important platform chemical, as a cheap feedstock for the synthesis of valuable chemicals. These chemicals can be formed in aqueous media through the glycerol electrooxidation reaction (GEOR) on the anode with hydrogen gas concurrently generated on the cathode. This thesis focuses on the GEOR in alkaline media on Pd and PdNi catalysts. The works compiled here evaluate the GEOR using electrochemical methods such as cyclic voltammetry, galvanostatic polarisation curves, chronoamperometry and chronopotentiometry. Pd and PdNi catalysts were fabricated through chemical synthesis, and electrodeposition onto Ni substrates. Singularly oriented Pd crystal facets were studied, showing those approximating Pd (111) as the most active. Similarly faceted bimetallic PdNi nanoparticles proved significantly more active than pure Pd. Effects of mass transport, studied for Pd/NiRDE and PdNi/NiRDE, indicated performance effects linked to diffusion and underutilisation of thicker catalyst layers. In aerated solutions, industrially relevant current densities were achieved on PdNi/Nifoam in concentrated electrolytes at elevated temperatures for extended periods. The analysis of glycerol oxidation products, formed during steady state measurements, was done using high performance liquid chromatography. The two major products were consistently shown to be glycerate and lactate. This work, covering many aspects of the GEOR, shows that Pd-based catalysts have potential for future industrial application.
|
|