In situ He+ irradiation of the double solid solution (Ti-0.5,Zr-0.5)(2)(Al-0.5,Sn-0.5)C MAX phase: Defect evolution in the 350-800 degrees C temperature range
-
- Tunca, B. (författare)
- SCK CEN, Belgium; Katholieke Univ Leuven, Belgium
-
- Greaves, G. (författare)
- Univ Huddersfield, England
-
- Hinks, J. A. (författare)
- Univ Huddersfield, England
-
visa fler...
-
- Persson, Per O A (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Vleugels, J. (författare)
- Katholieke Univ Leuven, Belgium
-
- Lambrinou, K. (författare)
- SCK CEN, Belgium; Univ Huddersfield, England
-
visa färre...
-
(creator_code:org_t)
- PERGAMON-ELSEVIER SCIENCE LTD, 2021
- 2021
- Engelska.
-
Ingår i: Acta Materialia. - : PERGAMON-ELSEVIER SCIENCE LTD. - 1359-6454 .- 1873-2453. ; 206
- Relaterad länk:
-
https://pure.hud.ac....
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Thin foils of the double solid solution (Zr-0.5,Ti-0.5)(2)(Al-0.5,Sn-0.5)C MAX phase were in situ irradiated in a transmission electron microscope (TEM) up to a fluence of 1.3 x 10(17) ions.cm(-2) (similar to 7.5 dpa), using 6 keV He+ ions. Irradiations were performed in the 350-800 degrees C temperature range. In situ and post-irradiation examination (PIE) by TEM was used to study the evolution of irradiation-induced defects as function of dose and temperature. Spherical He bubbles and string-like arrangements thereof, He platelets, and dislocation loops were observed. Dislocation loop segments were found to lie in non-basal-planes. At irradiation temperatures >= 450 degrees C, grain boundary tearing was observed locally due to He bubble segregation. However, the tears did not result in transgranular crack propagation. The intensity of specific spots in the selected area electron diffraction patterns weakened upon irradiation at 450 and 500 degrees C, indicating an increased crystal symmetry. Above 700 degrees C this was not observed, indicating damage recovery at the high end of the investigated temperature range. High-resolution scanning TEM imaging performed during the PIE of foils previously irradiated at 700 degrees C showed that the chemical ordering and nanolamination of the MAX phase were preserved after 7.5 dpa He+ irradiation. The size distributions of the He platelets and spherical bubbles were evaluated as function of temperature and dose. (C) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Ämnesord
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas