- Fu, Le, et al.
(författare)
-
Doping of tantalum, niobium, and hafnium in a translucent ZrO2-SiO2 nanocrystalline glass-ceramic
- 2022
-
Ingår i: Journal of the European Ceramic Society. - : Elsevier. - 0955-2219 .- 1873-619X. ; 42:4, s. 1731-1742
-
Tidskriftsartikel (refereegranskat)abstract
- The addition of dopant(s) is an effective strategy to regulate the microstructure and properties of ZrO2-based ceramics. In this study, we investigated the effects of ternary element alloying, namely tantalum (Ta), niobium (Nb), and hafnium (Hf) elements, on the microstructure and transformability of ZrO2 nanocrystallites in a ZrO2SiO2 nanocrystalline glass-ceramic (NCGC) during sintering and thermal treatments. The ternary dopants enhanced the transformability of tetragonal ZrO2 (t-ZrO2) nanocrystallites during sintering, i.e., the dopants acted as t-ZrO2 destabilizer. The Ta, Nb and Hf elements dissolved in ZrO2 nanocrystallites, forming ZrO2 solid solution. Meanwhile, lamella nanotwins were formed within many ZrO2 nanocrystallites. No obvious segregation of dopants was detected at ZrO2 grain boundaries. t-ZrO2 and monoclinic (m) ZrO2 nanocrystallites were metastable in thermal treatments process, with "t" to "m" and the reverse "m" to "t" polymorphic transformation occurred simultaneously. Meanwhile, t-ZrO2 and m-ZrO2 nanocrystallites had a great tendency to grow larger during thermal treatments.
|
|
2. |
- Fu, Le, et al.
(författare)
-
Understanding microstructure-mechanical properties relationship in ZrO2-SiO2 nanocrystalline glass-ceramics : The effect of ZrO2 content
- 2022
-
Ingår i: Materials Science & Engineering. - : Elsevier. - 0921-5093 .- 1873-4936. ; 840
-
Tidskriftsartikel (refereegranskat)abstract
- The content of crystalline phase plays a significant role in manipulating the microstructure and mechanical properties of glass-ceramics. This study aims at exploring the optimum content of crystalline phase in ZrO2-SiO2 nanocrystalline glass-ceramics (NCGCs) in terms of obtaining the highest mechanical properties. To this end, the mechanical properties of ZrO2-SiO2 NCGCs with 70 mol%, 75 mol%, 80 mol% ZrO2 were tested and compared with those of the previously prepared NCGCs with ZrO2 content ranging from 35 mol% to 65 mol%. Results showed that 65 mol% was the optimum content of ZrO2 in terms of obtaining the highest flexural strength. The flexural strength of NCGCs with ZrO2 content over 65 mol% was lower than that of the NCGCs with 65 mol% ZrO2. This was because the NCGC with 65 mol% ZrO2 had a homogenous microstructure, with ZrO2 nano crystallites homogeneously distributed in an amorphous SiO2 matrix. Whereas, when ZrO2 content was increased to 75 mol%, ZrO2 nanocrystallites were not homogeneously distributed in the SiO2 matrix anymore. The formation of SiO2 "holes/canyon " due to ZrO2 grain coalescence resulted in the decrease of flexural strength. The fracture mechanism and wear properties of the NCGCs were also investigated.
|
|
3. |
- Wang, Bohan, et al.
(författare)
-
Effects of dopants with various valences on densification behavior and phase composition of a ZrO2-SiO2 nanocrystalline glass-ceramic
- 2022
-
Ingår i: Ceramics International. - : Elsevier. - 0272-8842 .- 1873-3956. ; 48:7, s. 9495-9505
-
Tidskriftsartikel (refereegranskat)abstract
- Effects of dopants with different valences on the densification behavior and phase composition of a ZrO2-SiO2 nanocrystalline glass-ceramic (NCGC) during pressureless sintering were investigated in this study. The raw powder of Ca2+, La3+, Ce4+ and Ta5+ ions doped ZrO2-SiO2 (referred to as Ca-ZS, La-ZS, Ce-ZS, Ta-ZS, respectively) and pure ZrO2-SiO2 (PZS) sample were synthesized by sol-gel method, followed by pressureless sintering. Compared with the PZS sample, doping of Ca2+ and La3+ ions significantly promoted the densification of the NCGCs. The "densification promotion " effect was attributed to the formation of oxygen vacancies and the decrease of SiO2 viscosity due to doping of aliovalent cations. The dopants with various valences showed significant effects on the phase compositions of the NCGCs during sintering. Doping of Ca2+ ion accelerated the reaction kinetics between ZrO2 nanocrystallites and amorphous SiO2 to yield ZrSiO4. The La3+ ion acted as destabilizer of t-ZrO2, which resulted in a rapid tetragonal (t) to monoclinic (m) ZrO2 phase transformation during sintering, while in the Ta5+ and Ce4+ ions doped sample, the phase transformation occurred gradually. All the doping ions increased the lattice parameters and the volume of t-ZrO2 unit cell, while the effects of the doping ions on the lattice parameters of m-ZrO2 unit cell were more complex.
|
|