| 1. |
- Anyfantis, Dimitrios I., et al.
(författare)
-
Growth, Magnetic Anisotropies and Exchange Bias of Thin Ni0.95Fe0.05/NiFeO Multilayers
- 2022
-
Ingår i: Coatings. - : MDPI AG. - 2079-6412. ; 12:5
-
Tidskriftsartikel (refereegranskat)abstract
- Ni0.95Fe0.05/NiFeO multilayers were fabricated by radio frequency magnetron sputtering and natural oxidation. Doping of Ni by only 5 at. % Fe results in enhanced layering quality as X-ray reflectivity reveals. Due to magnetostatic anisotropy, the multilayers were found to be in-plane magnetized. The influence of mild thermal annealing (T = 525 K) on the magnetic properties of NiFe/NiFeO multilayers is also investigated. Annealing results in the enhancement of perpendicular magnetic anisotropy, mainly due to an increase in the uniaxial volume anisotropy term. Temperature-dependent hysteresis measurements between 4-400 K revealed considerable enhancement of coercivity and appearance of exchange bias effect.
|
|
| 2. |
- Barnasas, A., et al.
(författare)
-
Quantum confinement effects of thin ZnO films by experiment and theory
- 2020
-
Ingår i: Physica. E, Low-Dimensional systems and nanostructures. - : ELSEVIER. - 1386-9477 .- 1873-1759. ; 120
-
Tidskriftsartikel (refereegranskat)abstract
- Thin ZnO films with thickness ranging between 2 and 300 nm have been grown on quartz, Corning glass and Si (100) substrates by radio frequency magnetron sputtering. The film thickness was determined by pre-calibrated quartz balance with the help of x-ray reflectivity measurements. X-ray diffraction experiments revealed the formation of highly-textured hexagonal ZnO. Ultraviolet-visible light absorption spectroscopy has shown a "blue shift" of the direct band gap of ZnO. The experimental results are interpreted as evidences of quantum confinement effects. This is supported by theoretical predictions of the optical gap, which was calculated in the framework of effective mass approximation by solving the two particle (electron and hole) Hartree-Fock equations. The observed fair agreement between theoretical and experimental results corroborates the quantum confinement interpretation.
|
|
| 3. |
- Carstensen, Hauke, et al.
(författare)
-
Self-assembly and percolation in two dimensional binary magnetic colloids
- 2022
-
Ingår i: Soft Matter. - : Royal Society of Chemistry (RSC). - 1744-683X .- 1744-6848. ; 18:33, s. 6222-6228
-
Tidskriftsartikel (refereegranskat)abstract
- We study the self-assembly of branching-chain networks and crystals in a binary colloidal system with tunable interactions. The particle positions are extracted from microscopy images and order parameters are extracted by image processing and statistical analysis. With these, we construct phase diagrams with respect to particle density, ratio and interaction. In order to draw a more complete picture, we complement the experiments with computer simulations. We establish a region in the phase diagram, where bead ratios and interactions are symmetric, promoting percolated structures.
|
|
| 4. |
- Chioar, Ioan-Augustin, et al.
(författare)
-
Steering light with magnetic textures
- 2022
-
Ingår i: Applied Physics Letters. - : American Institute of Physics (AIP). - 0003-6951 .- 1077-3118. ; 120:3
-
Tidskriftsartikel (refereegranskat)abstract
- We study the steering of visible light using a combination of magneto-optical effects and the reconfigurability of magnetic domains in yttrium-iron garnet films. The spontaneously formed stripe domains are used as a field-controlled optical grating, allowing for active spatiotemporal control of light. We discuss the basic ideas behind the approach and provide a quantitative description of the field dependence of the obtained light patterns. Finally, we calculate and experimentally verify the efficiency of our magneto-optical grating.
|
|
| 5. |
- Čiučiulkaitė, Agnė, MSc, 1991-
(författare)
-
Dynamics in magnetic metamaterials
- 2021
-
Doktorsavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Metamaterials are artificially created structures with properties that are not found in nature. They can be tailored to achieve desired response to external excitations such as external electric and magnetic fields, as well as to enhance materials’ optical or magnetic activity. Magnetic metamaterials comprised of arrays of sub-micrometer sized magnetic elements, can be used for a range of different applications, such as magnonic crystals and building blocks for magnetic memory elements.In this work, pathways for tuning magnetization dynamics are explored. Different magnetic metamaterials containing arrays of sub-micrometer sized elements, refered to as nanomagnets, were used as model systems for these explorations. The nano-magnets comrising these arrays are of two kinds: XY-rotors, with a magnetization direction rotating freely in-plane of a disk, and Ising-like spins, pointing along either of the two allowed magnetization directions. The Ising-like spins can be realized in either in-plane or out-of-plane magnetized materials.Collective magnetization dynamics were investigated in square arrays of coupled nanomagnets. Studies revealed that nanomagnet’s magnetization state cannot always be approximated by a ridig mesospin approximation. Instead, it was demonstrated that upon an external perturbation, such as an external magnetic or thermal field, internal magnetization experience texture excitations. The observed texture excitations have implications on the nanomagnet coupling in an array.Arrays, where collective phenomena emerge via excited plasmon resonances, were used for investigations of light-induced dynamics processes. Studies revealed importance of an array design for the observation of magneto-optical activity enhancement and more eÿcient ultrafast magnetization dynamics. It was reported that in arrays containing truncated Au nanocones with TbCo tip, enhancement of TbCo demagnetization can be achieved via resonant light illumination.Utilizing the array concept and magnetic anisotropy of a material, it is possible to create metamaterials, where a range of magnetization dynamics regimes can be investigated. Inter-element spacing defines on which lengthscale the nanomagnets will be coupled and which effects can be utilized for tuning system’s magneto-optical response and excited magnetization dynamics.
|
|
| 6. |
- Ciuciulkaite, Agne, MSc, 1991-, et al.
(författare)
-
Magnetic and all-optical switching properties of amorphous TbxCo100-x alloys
- 2020
-
Ingår i: Physical Review Materials. - : American Physical Society (APS). - 2475-9953. ; 4:10
-
Tidskriftsartikel (refereegranskat)abstract
- Amorphous TbxCo100-x magnetic alloys exhibit a list of intriguing properties, such as perpendicular magnetic anisotropy, high magneto-optical activity, and magnetization switching using ultrashort optical pulses. Varying the Tb:Co ratio in these alloys allows for tuning properties such as the saturation magnetic moment, coercive field, and the performance of light-induced magnetization switching. In this paper, we investigate the magnetic, optical, and magneto-optical properties of various TbxCo100-x thin-film alloy compositions. We report on the effect the choice of different seeding layers has on the structural and magnetic properties of TbxCo100-x layers. We also demonstrate that for a range of alloys, deposited on fused silica substrates, with Tb content of 24-30 at. %, helicity-dependent all-optical switching of magnetization can be achieved, albeit in a multishot framework. We explain this property to arise from the helicity-dependent laser-induced magnetization on the Co sublattice due to the inverse Faraday effect. Our paper provides an insight into material aspects for future potential hybrid magnetoplasmonic TbCo-based architectures.
|
|
| 7. |
- Denoel, Fernand
(författare)
-
Electronic and magnetic properties of Tsai quasicrystals and their approximants under pressure
- 2022
-
Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Quasicrystals constitute a special category of crystals exhibiting long-range order without periodicity. This strange feature allows them to exhibit rotational symmetries prohibited in regular crystals, such as 5-, 8-, 10- or 12-fold symmetry. Amongst them, icosahedral quasicrystals are the only type that is aperiodic along all 3 dimensions. The present work will focus on Tsai-Type quasicrystals and their approximants, which are the most studied type of icosahedral quasicrystals. We will introduce how they can be generated froma hyperspace perspective, their exotic structure and how it relates to their physical properties. Pressure is a key parameter which can be used to alter the condensed matter properties of a material. By reducing the size of samples and using diamond anvil cells, it is possible to obtain the highest experimentally achievable pressures and collect informations such as magnetization, electrical resistivity or Raman signal. This work will introduce the specialized diamond anvil cells we used to investigate electron transport and magnetization under pressure, explain in details how to circumvent the most common difficulties arising with high pressure setups. and describe how high pressure affects Tsai quasicrystals and approximants in terms of structure and magnetic properties.
|
|
| 8. |
- Dorri, Samira, 1988-
(författare)
-
Magnetron Sputter Epitaxy of CrB2/TiB2 Diboride Superlattice Thin Films
- 2024
-
Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Artificial superlattices with their exceptional properties have been popular in a broad range of applications such as electronic, magnetic, optical, and hard coating. Another potential application for single crystal artificial superlattices is highly efficient interference neutron optics, owing to an ultimate interface width of just ±½ atomic layer. Moreover, studies of superlattices have been instrumental in understanding the hardening mechanisms in transition metal nitrides and carbides while such studies on transition metal diborides is lacking, despite extensive studies on monolithic transition metal diboride thin films.This work is an initiative to grow CrB2/TiB2 (0001) diboride superlattices epitaxially onto Al2O3 (0001) substrates by direct current magnetron sputter epitaxy implementing two different approaches; compound diboride targets, and co-sputtering of a metal target with a compound target. Effects of substrate temperature, B stoichiometry (B/TM ratio), modulation period Λ = DCrB2 + DTiB2, layer thickness ratio , and relative applied power to magnetrons on the structural and interface quality of superlattices are studied and discussed.Using compound targets, superlattices with thickness ratio Γ = 0.3 and modulation periods Λ between 1 and 10 nm, and with Λ = 6 nm and thickness ratios between 0.2 to 0.8 were synthesized at the optimum sputter gas pressure of pAr = 4 mTorr and a substrate temperature of 600 °C. It is found that superlattices with Λ = 6 nm and Γ in the range of 0.2-0.4 exhibit the highest structural quality. However, B segregation in the over-stoichiometric TiBy layers (y > 2), grown from TiB2 compound target, results in narrow epitaxial superlattice columnar growth with structurally distorted B-rich boundaries. By co-sputtering from Ti and TiB2 targets, y could be reduced from 3.3 to 0.9 in TiBy layers through controlling the relative applied target power. Co-sputtered TiBy single layers and superlattices were grown at substrate temperatures between 600 and 900 °C. 300-nm-thick TiB2.3 single layers grown at 750 °C exhibited epitaxial domains about 10x larger than non-co-sputtered films.A significant enhancement for close-tostoichiometry CrB1.7/TiB2.3 superlattices with modulation periods Λ = 6 nm was achieved at 750 °C. X-ray diffraction, time of flight elastic recoil detection analysis, scanning transmission electron microscopy, electron energy loss spectroscopy, selected area electron diffraction, and nano-indentation are used for characterization.
|
|
| 9. |
- Gemma, Ryota, et al.
(författare)
-
The impact of nanoscale compositional variation on the properties of amorphous alloys
- 2020
-
Ingår i: Scientific Reports. - : NATURE PUBLISHING GROUP. - 2045-2322. ; 10:1
-
Tidskriftsartikel (refereegranskat)abstract
- The atomic distribution in amorphous FeZr alloys is found to be close to random, nevertheless, the composition can not be viewed as being homogenous at the nm-scale. The spatial variation of the local composition is identified as the root of the unusual magnetic properties in amorphous Fe1-xZrx alloys. The findings are discussed and generalised with respect to the physical properties of amorphous and crystalline materials.
|
|
| 10. |
- Ignatova, K., et al.
(författare)
-
Reversible exchange bias in epitaxial V2O3/Ni hybrid magnetic heterostructures
- 2022
-
Ingår i: Journal of Physics. - : Institute of Physics (IOP). - 0953-8984 .- 1361-648X. ; 34:49
-
Tidskriftsartikel (refereegranskat)abstract
- In this work we present a temperature and angular dependent study of the structural and magnetic properties in highly crystalline V2O3/Ni/Zr magnetic heterostructure films. Our investigation focuses on the coupling between the ferromagnetic Ni layer and V2O3 layer which undergoes an antiferromagnetic/paramagnetic phase transition coupled to the structural phase transition of the material at around 150 K. Structural investigations using x-ray diffraction reveal highly crystalline films of a quality which has previously not been reported in the literature. The Ni layers display an absence of in-plane magnetic anisotropy owing to the highly textured (1 1 1) layering of the Ni films on the underlying V2O3(0 0 0 1) oriented layer. During the transition we observe a strain related enhancement of the coercivity and the onset of a weak exchange bias for cooling under an external magnetic field. Heating the films to above the transition temperature, the exchange bias in the Ni is removed and can be reversed upon subsequent cooling under an inverted external magnetic field. Using temperature dependent polarized neutron reflectometry we investigate the film structure at the interface, capturing the magnetic and nuclear profiles.
|
|