1. |
- Kirsebom, O. S., et al.
(author)
-
Precise and accurate determination of the B-8 decay spectrum
- 2011
-
In: Physical Review C - Nuclear Physics. - 2469-9985 .- 2469-9993. ; 83:6
-
Journal article (peer-reviewed)abstract
- Accurate measurements of the B-8 neutrino spectrum are important for the interpretation of solar neutrino data. Experimentally, the B-8 neutrino spectrum can be obtained from the measurement of the beta-delayed alpha spectrum. We report on an alpha-alpha coincidence measurement performed at the IGISOL facility in Jyvaskyla, Finland. Our measurement allows extensive cross-checks to be performed and gives a more intense neutrino spectrum at high energies compared to the present standard. The deviation reaches 4% at the end point of the spectrum. Below 11 MeV, the deviation is less than 1%.
|
|
2. |
|
|
3. |
- Penttila, H., et al.
(author)
-
Independent Isotopic Product Yields in 25 MeV and 50 MeV Charged Particle Induced Fission of U-238 and Th-232
- 2014
-
In: Nuclear Data Sheets. - : Elsevier BV. - 0090-3752 .- 1095-9904. ; 119, s. 334-337
-
Journal article (peer-reviewed)abstract
- Independent isotopic yields for most elements from Zn to La in 25-MeV proton-induced fission of U-238 and Th-232 have been determined at the IGISOL facility in the University of Jyvaskyla. In addition, isotopic yields for Zn, Ga, Rb, Sr, Zr, Pd and Xe in 50-MeV proton-induced fission of U-238 and for Zn, Ga, Rb, Sr, Cd and In in 25-MeV deuterium-induced fission of U-238 have been measured. The utilised technique recently developed at the University of Jyvaskyla, is based on a combination of the ion guide technique and the ability of a Penning trap to unambiguously identify the isotopes by their atomic mass. Since the yields are determined by ion counting, no prior knowledge beyond the mass and half-life of the isotopes was needed for the measurements.
|
|
4. |
- Shafeie, Samrand, 1984-, et al.
(author)
-
Phase formation, crystal structures and magnetic properties of perovskite-type phases in the system La2Co1+z(MgxTi1-x)1-zO6
- 2011
-
In: Journal of Solid State Chemistry. - : Elsevier BV. - 0022-4596 .- 1095-726X. ; 184:1, s. 177-190
-
Journal article (peer-reviewed)abstract
- Perovskite-type cobaltates in the system La(2)Co(1+z) (Mg(x)Ti(1-x))(1-z)O(6) were studied for z=0 <= x <= 0.6 and 0 <= x <= 0.9, using X-ray and neutron powder diffraction, electron diffraction (ED), magnetic susceptibility measurements and X-ray absorption near-edge structure (XANES) spectroscopy. The samples were synthesised using the citrate route in air at 1350 degrees C. The space group symmetry of the structure changes from P2(1)/n via Pbnm to R (3) over barc with both increasing Mg content and increasing Co content. The La(2)Co(Mg(x)Ti(1-x))O(6) (z=0) compounds show anti-ferromagnetic couplings of the magnetic moments for the Co below 15 K for x=0, 0.1 and 0.2. XANES spectra show for the compositions 0 <= x <= 0.5 a linear decrease in the L(3)/(L(3)+ L(2))Co-L(2.3) edge branching ratio with x, in agreement with a decrease of the average Co ion spin-state, from a high-spin to a lower-spin-state, with decreasing nominal Co(2+) ion content.
|
|