| 1. |
- Li, Yan-Ling, et al.
(författare)
-
Formation of Nanofoam carbon and re-emergence of Superconductivity in compressed CaC6
- 2013
-
Ingår i: Scientific Reports. - : Springer Science and Business Media LLC. - 2045-2322. ; 3, s. 3331-
-
Tidskriftsartikel (refereegranskat)abstract
- Pressure can tune material's electronic properties and control its quantum state, making some systems present disconnected superconducting region as observed in iron chalcogenides and heavy fermion CeCu2Si2. For CaC6 superconductor (T-c of 11.5 K), applying pressure firstTc increases and then suppresses and the superconductivity of this compound is eventually disappeared at about 18 GPa. Here, we report a theoretical finding of the re-emergence of superconductivity in heavily compressed CaC6. The predicted phase III (space group Pmmn) with formation of carbon nanofoam is found to be stable at wide pressure range with a Tc up to 14.7 K at 78 GPa. Diamond-like carbon structure is adhered to the phase IV (Cmcm) for compressed CaC6 after 126 GPa, which has bad metallic behavior, indicating again departure from superconductivity. Re-emerged superconductivity in compressed CaC6 paves a new way to design new-type superconductor by inserting metal into nanoporous host lattice.
|
|
| 2. |
- Li, Yan-Ling, et al.
(författare)
-
Pressure-induced superconductivity in CaC2
- 2013
-
Ingår i: Proceedings of the National Academy of Sciences of the United States of America. - : National Academy of Sciences. - 0027-8424 .- 1091-6490. ; 110:23, s. 9289-9294
-
Tidskriftsartikel (refereegranskat)abstract
- Carbon can exist as isolated dumbbell, 1D chain, 2D plane, and 3D network in carbon solids or carbon-based compounds, which attributes to its rich chemical binding way, including sp-, sp(2)-, and sp(3)-hybridized bonds. sp(2)-hybridizing carbon always captures special attention due to its unique physical and chemical property. Here, using an evolutionary algorithm in conjunction with ab initio method, we found that, under compression, dumbbell carbon in CaC2 can be polymerized first into 1D chain and then into ribbon and further into 2D graphite sheet at higher pressure. The C2/m structure transforms into an orthorhombic Cmcm phase at 0.5 GPa, followed by another orthorhombic Immm phase, which is stabilized in a wide pressure range of 15.2-105.8 GPa and then forced into MgB2-type phase with wide range stability up to at least 1 TPa. Strong electron-phonon coupling. in compressed CaC2 is found, in particular for Immm phase, which has the highest lambda value (0.562-0.564) among them, leading to its high superconducting critical temperature T-c (7.9 similar to 9.8 K), which is comparable with the 11.5 K value of CaC6. Our results show that calcium not only can stabilize carbon sp(2) hybridization at a larger range of pressure but also can contribute in superconducting behavior, which would further ignite experimental and theoretical interest in alkaline-earth metal carbides to uncover their peculiar physical properties under extreme conditions.
|
|