1.
  • Mayrhofer, Paul H., et al. (författare)
  • Structure evolution of Cr-Al-N hard coatings
  • 2006
  • Ingår i: Society of Vacuum Coaters 49th Annual Technical Conference,2006.
  • Konferensbidrag (övrigt vetenskapligt/konstnärligt)
  •  
2.
  • Willmann, Herbert, et al. (författare)
  • Hardness evolution of Al-Cr-N coatings under thermal load
  • 2008
  • Ingår i: Journal of Materials Research. - 0884-2914 .- 2044-5326. ; 23:11, s. 2880-2885
  • Tidskriftsartikel (refereegranskat)abstract
    • Microstructure and hardness evolution of arc-evaporated single-phase Cubic Al0.56Cr0.44N and Al0.68Cr0.32N coatings have been investigated after thermal treatment in Ar atmosphere. Based on a combination of differential scanning calorimetry and x-ray diffraction studies, We Can Conclude that Al0.56Cr0.44N undergoes only small structural changes without any decomposition for annealing temperatures T-a <= 900 degrees C. Consequently, the hardness decreases only marginally from the as-deposited value of 30.0 +/- 1.1 GPa to 29.4 +/- 0.9 GPa with T-a increasing to 900 degrees C, respectively. The film with higher Al content (Al0.68Cr0.32N) exhibits formation of hexagonal (h) AlN at T-a >= 700 degrees C, which occurs preferably at grain boundaries as identified by analytical transmission electron microscopy. Hence, the hardness increases from the as-deposited value of 30.1 +/- 1.3 GPa to 31.6 +/- 1.4 GPa with T-a = 725 degrees C. At higher temperatures, where the size and volume fraction of the h-AlN phase increases, the hardness decreases to 27.5 +/- 1.0 GPa with T-a = 900 degrees C.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-2 av 2

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy