  • Ghadami Yazdi, Milad, et al. (författare)
  • Structure dependent effect of silicon on the oxidation of Al(111) and Al(100)
  • 2019
  • Ingår i: Surface Science. - : Elsevier. - 0039-6028 .- 1879-2758. ; 684, s. 1-11
  • Tidskriftsartikel (refereegranskat)abstract
    • The effect of sub-monolayer silicon on the oxidation of Al(111) and Al(100) surfaces was investigated using X-ray Photoelectron Spectroscopy (XPS) and density functional theory (DFT) calculations. On both surfaces the adatom site is preferred over substituting Si into the Al-lattice; on Al(100) the four fold hollow site is vastly favored whereas on Al(111) bridge and hollow sites are almost equal in energy. Upon O 2 exposure, Si is not oxidized but buried at the metal/oxide interface under the growing aluminum oxide. On Al(111), Si has a catalytic effect on both the initial oxidation by aiding in creating a higher local oxygen coverage in the early stages of oxidation and, in particular, at higher oxide coverages by facilitating lifting Al from the metal into the oxide. The final oxide, as measured from the Al2p intensity, is 25–30% thicker with Si than without. This observation is valid for both 0.1 monolayer (ML) and 0.3 ML Si coverage. On Al(100), on the other hand, at 0.16 ML Si coverage, the initial oxidation is faster than for the bare surface due to Si island edges being active in the oxide growth. At 0.5 ML Si coverage the oxidation is slower, as the islands coalesce and he amount of edges reduces. Upon oxide formation the effect of Si vanishes as it is overgrown by Al 2 O 3 , and the oxide thickness is only 6% higher than on bare Al(100), for both Si coverages studied. Our findings indicate that, in addition to a vanishing oxygen adsorption energy and Mott potential, a detailed picture of atom exchange and transport at the metal/oxide interface has to be taken into account to explain the limiting oxide thickness.
  •  
3.
  • Yazdi, Milad Ghadami, et al. (författare)
  • Surface modified composite nanofibers for the removal of indigo carmine dye from polluted water
  • 2018
  • Ingår i: RSC Advances. - : Royal Society of Chemistry. - 2046-2069. ; 8:43, s. 24588-24598
  • Tidskriftsartikel (refereegranskat)abstract
    • Surface coated magnetite nanoparticles (Fe3O4 NPs) with 3-mercaptopropionic acid were immobilized on amidoximated polyacrilonitrile (APAN) nanofibers using electrospinning followed by crosslinking. The prepared composite nanofibers were characterized with Scanning Electron Microscopy (SEM), and Fourier Transform Infrared analysis (FTIR). The composite nanofiber was evaluated for the removal of indigo carmine dye from aqueous solutions. The effects of contact time, initial dye concentration, solution pH and adsorption equilibrium isotherms were studied. The adsorption of indigo carmine was found to be greatly affected by solution pH. The maximum loading capacity was determined to be 154.5 mg g(-1) at pH = 5. The experimental kinetic data were fitted well using a pseudo-first order model. The adsorption isotherm studies showed that the adsorption of indigo carmine fits well with the Langmuir model. The reuse of the composite nanofiber was also investigated in which more than 90% of indigo carmine was recovered in 5 min. The results of stability studies showed that the adsorption efficiency can remain almost constant (90%) after five consecutive adsorption/desorption cycles.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-3 av 3

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy