SwePub
Tyck till om SwePub Sök här!
Sök i SwePub databas

  Utökad sökning

Träfflista för sökning "WFRF:(Nikas A) srt2:(2020-2023)"

Sökning: WFRF:(Nikas A) > (2020-2023)

  • Resultat 1-3 av 3
Sortera/gruppera träfflistan
   
NumreringReferensOmslagsbildHitta
1.
  •  
2.
  • Wu, Lang, et al. (författare)
  • An integrative multi-omics analysis to identify candidate DNA methylation biomarkers related to prostate cancer risk.
  • 2020
  • Ingår i: Nature Communications. - : Springer Science and Business Media LLC. - 2041-1723. ; 11:1
  • Tidskriftsartikel (refereegranskat)abstract
    • It remains elusive whether some of the associations identified in genome-wide association studies of prostate cancer (PrCa) may be due to regulatory effects of genetic variants on CpG sites, which may further influence expression of PrCa target genes. To search for CpG sites associated with PrCa risk, here we establish genetic models to predict methylation (N = 1,595) and conduct association analyses with PrCa risk (79,194 cases and 61,112 controls). We identify 759 CpG sites showing an association, including 15 located at novel loci. Among those 759 CpG sites, methylation of 42 is associated with expression of 28 adjacent genes. Among 22 genes, 18 show an association with PrCa risk. Overall, 25 CpG sites show consistent association directions for the methylation-gene expression-PrCa pathway. We identify DNA methylation biomarkers associated with PrCa, and our findings suggest that specific CpG sites may influence PrCa via regulating expression of candidate PrCa target genes.
  •  
3.
  • Vilardell, A. M., et al. (författare)
  • B2-structured Fe3Al alloy manufactured by laser powder bed fusion : Processing, microstructure and mechanical performance
  • 2023
  • Ingår i: Intermetallics (Barking). - : Elsevier. - 0966-9795 .- 1879-0216. ; 156
  • Tidskriftsartikel (refereegranskat)abstract
    • Prealloyed Fe3Al was successfully manufactured by laser powder bed fusion. The best set of process parameters led to parts with a relative density of 99.5 %, a surface roughness, Sa, of 31.5 ± 5.6 μm and a hardness of 319 ± 14 HV0.1. Its microstructure as well as its mechanical properties at room and high temperatures were analyzed. The results of the chemical composition showed minor variations in aluminum content oscillating between 21 and 28 at.% along the melt pool. Additionally, elongated grains were observed to grow parallel to the building direction, as well as the development of a weak 001 texture along the building direction. The mechanical properties were influenced by the temperature. Compression tests showed a loss in strength with the increase in temperature, from a yield strength of 621 ± 40 MPa at room temperature to 89 ± 20 MPa at 650 °C. Reciprocating sliding wear tests showed that fragmentation of the intermetallic at room temperature occurs, whereas plastic deformation dominated at higher temperatures. For all temperatures, tribochemical wear was also present due to the oxidation of wear debris. 
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-3 av 3

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy