- Qin, Gang, et al.
(författare)
-
A novel face-centered-cubic high-entropy alloy strengthened by nanoscale precipitates
- 2019
-
Ingår i: Scripta Materialia. - : PERGAMON-ELSEVIER SCIENCE LTD. - 1359-6462 .- 1872-8456. ; 172, s. 51-55
-
Tidskriftsartikel (refereegranskat)abstract
- A new single-phase face-centered-cubic (FCC) Co9Cr7Cu36Mn25Ni23 [atomic percent, similar hereinafter] high-entropy alloy (HEA) was prepared by arc melting. A uniform distribution of nanometer-sized precipitates was achieved. The tensile yield strength, ultimate tensile strength, and elongation were 401 MPa, 700 MPa, and 36%, respectively. The energy-dispersive spectrometer results showed that the nano-precipitates were rich in Co and Cr elements. Moreover, the crystal-forming behavior and the nanoscale-precipitates-forming mechanism were revealed. Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
|
|