| 1. |
|
|
| 2. |
- Dammström, S., et al.
(författare)
-
On the interactions between cellulose and xylan, a biomimetic simulation of the hardwood cell wall
- 2009
-
Ingår i: BioResources. - 1930-2126. ; 4:1, s. 3-14
-
Tidskriftsartikel (refereegranskat)abstract
- The plant cell wall exhibits a hierarchical structure, in which the organization of the constituents on different levels strongly affects the mechanical properties and the performance of the material. In this work, the interactions between cellulose and xylan in a model system consisting of a bacterial cellulose/glucuronoxylan (extracted from aspen, Populus tremula) have been studied and compared to that of a delignified aspen fiber material. The properties of the materials were analyzed using Dynamical Mechanical Analysis (DMA) with moisture scans together with dynamic Infra Red -spectroscopy at dry and humid conditions. The results showed that strong interactions existed between the cellulose and the xylan in the aspen holocellulose. The same kinds of interactions were seen in a water-extracted bacterial cellulose/xylan composite, while unextracted material showed the presence of xylan not interacting with the cellulose. Based on these findings for the model system, it was suggested that there is in hardwood one fraction of xylan that is strongly associated with the cellulose, taking a similar role as glucomannan in softwood.
|
|
| 3. |
- Modén, Carl S., 1979-
(författare)
-
Transverse anisotropy in softwoods : Modelling and experiments
- 2006
-
Licentiatavhandling (övrigt vetenskapligt/konstnärligt)abstract
- Transverse anisotropy is an important phenomenon of practical and scientific interest. Although the presence of ray tissue explains the high radial modulus in many hardwoods, experimental data in the literature shows that this is not the case for pine. It is possible that anisotropy in softwoods may be explained by the cellular structure and associated deformation mechanisms. An experimental approach was developed by which local radial modulus in spruce was determined at sub-annual ring scale. Digital speckle photography (DSP) was used, and the density distribution was carefully characterized using x-ray densitometry and the SilviScan apparatus. A unique set of data was generated for radial modulus versus a wide range of densities. This was possible since earlywood density shows large density variations in spruce. Qualitative comparison was made between data and predictions from stretching and bending honeycomb models. The hypothesis for presence of cell wall stretching was supported by data. A model for wood was therefore developed where both cell wall bending and stretching are included. The purpose was a model for predictions of softwood moduli over a wide range of densities. The relative importance of the deformation mechanisms was investigated in a parametric study. A two-phase model was developed and radial and tangential moduli were predicted. Comparison with experimental data showed good agreement considering the nature of the model (density is the only input parameter). Agreement is much better than for a regular honeycomb model. According to the model, cell wall bending dominates at both low and high densities during tangential loading. In radial loading, cell wall stretching dominates at higher densities.
|
|
| 4. |
- Stevanic, Jasna S., et al.
(författare)
-
Orientation of the wood polymers in the cell wall of spruce wood fibres
- 2009
-
Ingår i: Holzforschung. - 0018-3830 .- 1437-434X. ; 63:5, s. 497-503
-
Tidskriftsartikel (refereegranskat)abstract
- The mechanical and physical properties of wood fibres depend to a large extent on the orientation of the polymers, mainly the cellulose microfibrils, within the supramolecular structure of the cell wall. Under moist conditions, the arrangement within the polymer matrix may play a dominant role for mechanical properties in general and, especially, in the transverse direction. In this context, it is of special interest to determine the orientation of glucomannan and xylan, being the essential components of softwood hemicelluloses, and of lignin in wood fibres. Fourier transform infrared (FTIR) microscopy was used to examine the orientation of the main wood polymers in transversal and longitudinal direction of spruce fibres. We investigated fibres made from a thermomechanical pulp, in which the outer fibre wall layers were removed by mechanical action, and chemically delignified fibres. The polarised FTIR measurements indicated that glucomannan and xylan appear to have a parallel orientation with regard to the orientation of cellulose and, in all probability, an almost parallel orientation with regard to the fibre axis. Lignin was found to be less oriented in the fibre wall, although its arrangement is not fully isotropic. In the longitudinal direction of the fibres, there were no significant changes in the molecular orientation of the studied polymers.
|
|