| 1. |
- Dainiak, Maria B, et al.
(författare)
-
Gelatin-fibrinogen cryogel dermal matrices for wound repair: Preparation, optimisation and in vitro study.
- 2010
-
Ingår i: Biomaterials. - : Elsevier BV. - 1878-5905 .- 0142-9612. ; 31, s. 67-76
-
Tidskriftsartikel (refereegranskat)abstract
- Macroporous sponge-like gelatin-fibrinogen (Gl-Fg) scaffolds cross-linked with different concentrations (0.05-0.5%) of glutaraldehyde (GA) were produced using cryogelation technology, which allows for the preparation of highly porous scaffolds without compromising their mechanical properties, and is a more cost-efficient process than freeze-drying. The produced Gl-Fg-GA(X) scaffolds had a uniform interconnected open porous structure with a porosity of up to 90-92% and a pore size distribution of 10-120mum. All of the obtained cryogels were elastic and mechanically stable, except for the Gl-Fg-GA(0.05) scaffolds. Swelling kinetics and degradation rate, but not the porous structure of the cryogels, were strongly dependent on the degree of cross-linking. A ten-fold increase in the degree of cross-linking resulted in an almost 80-fold decrease in the rate of degradation in a solution of protease. Cryogels were seeded with primary dermal fibroblasts and the densities observed on the surface, plus the expression levels of collagen types I and III observed 5 days post-seeding, were similar to those observed on a control dermal substitute material, Integra((R)). Fibroblast proliferation and migration within the scaffolds were relative to the GA content. Glucose consumption rate was 3-fold higher on Gl-Fg-GA(0.1) than on Gl-Fg-GA(0.5) cryogels 10 days post-seeding. An enhanced cell motility on cryogels with reducing GA crosslinking was obtained after long time culture. Particularly marked cell infiltration was seen in gels using 0.1% GA as a crosslinker. The scaffold started to disintegrate after 42 days of in vitro culturing. The described in vitro studies demonstrated good potential of Gl-Fg-GA(0.1) scaffolds as matrices for wound healing.
|
|
| 2. |
- Ivanov, Alexander, et al.
(författare)
-
Evaluation of boronate-containing polymer brushes and gels as substrates for carbohydrate-mediated adhesion and cultivation of animal cells.
- 2010
-
Ingår i: Colloids and Surfaces. B, Biointerfaces. - : Elsevier BV. - 1873-4367 .- 0927-7765. ; 75, s. 510-519
-
Tidskriftsartikel (refereegranskat)abstract
- Boronate-containing thin polyacrylamide gels (B-Gel), polymer brushes (B-Brush) and chemisorbed organosilane layers (B-COSL) were prepared on the surface of glass slides and studied as substrates for carbohydrate-mediated cell adhesion. B-COSL- and B-Brush-modified glass samples exhibited multiple submicron structures densely and irregularly distributed on the glass surface, as found by scanning electron microscopy and atomic force microscopy. B-Gel was ca. 0.1mm thick and contained pores with effective size of 1-2mum in the middle and of 5-20mum on the edges of the gel sample as found by confocal laser scanning microscopy. Evidence for the presence of phenylboronic acid in the samples was given by time-of-flight secondary ion mass-spectrometry (ToF SIMS), contact angle measurements performed in the presence of fructose, and staining with Alizarin Red S dye capable of formation specific, fluorescent complexes with boronic acids. A comparative study of adhesion and cultivation of animal cells on the above substrates was carried out using murine hybridoma M2139 cell line as a model. M2139 cells adhered to the substrates in the culture medium without glucose or sodium pyruvate at pH 8.0, and then were cultivated in the same medium at pH 7.2 for 4 days. It was found that the substrates of B-Brush type were superior both regarding cell adhesion and viability of the adhered cells, among the substrates studied. MTT assay confirmed proliferation of M2139 cells on B-Brush substrates. Some cell adhesion was also registered in the macropores of B-Gel substrate. The effects of surface microstructure of the boronate-containing polymers on cell adhesion are discussed. Transparent glass substrates grafted with boronate-containing copolymers offer good prospects for cell adhesion studies and development of cell-based assays.
|
|