| 1. |
- Brueckner, Frank, et al.
(författare)
-
Phenomena in multi-material fabrication using laser metal deposition
- 2019
-
Ingår i: Laser 3D Manufacturing VI. - : SPIE - The International Society for Optics and Photonics.
-
Konferensbidrag (refereegranskat)abstract
- Additive Manufacturing (AM) processes as Laser Metal Deposition (LMD) addresses various benefits such as the build-up of complex shaped parts, the possibility of functional integration, reduced lead times or the use of difficult machinable materials compared to conventional manufacturing possibilities. Beside mentioned advantages, the use of more than one material in a component strongly increases the field of applications. Similar to structures in nature, multi-material arrangements can be realized by (I) sharp intersections from one material to the other (e. g. in the case of a thin corrosion protection), (II) graded structures enabling smoother material transitions (e. g. dissimilar materials joined together without defects), (III) composite structures with enclosed particles in a matrix material as well as by (IV) in-situ alloying of different material compositions. Due to varying material properties (e.g. thermo-physical, mechanical, optical), the combination of materials often requires a detailed investigation of occurring process phenomena and well-chosen modifications of the process regimes. Within this paper, (a) the right material feeding as well as powder interaction between various materials in Laser Metal Deposition, (b) the suitable selection of laser wavelengths for different materials, (c) process window adjustments by means of additional sensor equipment, (d) limitations of material combinations as well as (e) results and material characterization of multi-material parts are discussed. Phenomena are discussed by means of exemplary industrial applications, e.g. from the jet engine or medical business.
|
|
| 2. |
- Mueller, Michael, et al.
(författare)
-
Microstructural, mechanical, and thermo-physical characterization of hypereutectic AlSi40 fabricated by selective laser melting
- 2019
-
Ingår i: Journal of laser applications. - : Laser Institute of America. - 1042-346X .- 1938-1387. ; 31:2
-
Tidskriftsartikel (refereegranskat)abstract
- The powder bed additive manufacturing process selective laser melting (SLM) enables designers and engineers to overcome restrictions of conventional manufacturing technologies. The potential of fabricating complex lightweight structures and processing advanced materials is a key feature for enhancing further development of high performance components for space applications. Due to a high specific stiffness and a thermal expansion coefficient very close to electroless nickel, which is an advantageous optical coating material, the hypereutectic aluminum-silicon alloy AlSi40 shows great potential for the manufacturing of optical mirrors for space applications. In prior investigations, Hilpert et al.showed the feasibility to process AlSi40 by SLM [E. Hilpert and S. Risse, Materials Science & Technology Conference and Exhibition MS&T'15, Columbus, Ohio, 4–8 October 2015(Association for Iron & Steel Technology, Warrendale, PA, 2015) and E. Hilpert, “Struktur und Eigenschaften von additiv gefertigten hypereutektischen Aluminum-Siliciumlegierungen,” in Werkstoffwoche 2017, Dresden, Germany, 28 September 2017 (Deutsche Gesellschaft für Materialkunde e.V., Berlin, 2017)]. Nevertheless, in order to qualify this material for space applications, the manufacturing process and fabricated samples need to be thoroughly investigated in terms of microstructural, mechanical, as well as thermo-physical characterization. The authors present results of the SLM process development for manufacturing dense AlSi40 samples with a relative density above 99.50%. The effect of various process parameters, such as hatch distance, preheating, and scanning strategy, on the formation of defects was investigated by destructive [e.g., optical microscopy (OM)] and nondestructive (e.g., computed tomography) testing. In addition, the effect of several thermal post-treatments on the AlSi40 microstructure was profoundly analyzed by multiple methods such as OM, scanning electron microscopy, and energy dispersive x-ray spectroscopy analysis. Moreover, mechanical and thermo-physical testing of manufactured specimens was conducted to provide material characteristics for component design. In conclusion, the determined material properties of AlSi40 samples fabricated by SLM were compared to bulk material properties. The gained knowledge and testing data were evaluated in order to identify correlations and dependencies.
|
|