| 1. |
- Afrasiabi, Roodabeh, et al.
(författare)
-
Microwave mediated synthesis of semiconductor quantum dots
- 2012
-
Ingår i: Physica Status Solidi. C, Current topics in solid state physics. - : Wiley. - 1610-1634 .- 1610-1642. ; 9:7, s. 1551-1556
-
Tidskriftsartikel (refereegranskat)abstract
- Colloidal quantum dots (QD) have tuneable optoelectronic properties and can be easily handled by simple solution processing techniques, making them very attractive for a wide range of applications. Over the past decade synthesis of morphology controlled high quality (crystalline, monodisperse) colloidal QDs by thermal decomposition of organometallic precursors has matured and is well studied. Recently, synthesis of colloidal QDs by microwave irradiation as heating source is being studied due to the inherently different mechanisms of heat transfer, when compared to solvent convection based heating. Under microwave irradiation, polar precursor molecules directly absorb the microwave energy and heat up more efficiently. Here we report synthesis of colloidal II-VI semiconductor QDs (CdS, CdSe, CdTe) by microwave irradiation and compare it with conventional synthesis based on convection heating. Our findings show that QD synthesis by microwave heating is more efficient and the chalcogenide precursor strongly absorbs the microwave radiation shortening the reaction time and giving a high reaction yield.
|
|
| 2. |
- Akman, O., et al.
(författare)
-
Magnetic metal nanoparticles coated polyacrylonitrile textiles as microwave absorber
- 2013
-
Ingår i: Journal of Magnetism and Magnetic Materials. - : Elsevier BV. - 0304-8853 .- 1873-4766. ; 327, s. 151-158
-
Tidskriftsartikel (refereegranskat)abstract
- Polyacrylonitrile (PAN) textiles with 2 mm thickness are coated with magnetic nanoparticles in coating baths with Ni, Co and their alloys via an electroless metal deposition method. The crystal structure, morphology and magnetic nature of composites are investigated by X-ray Powder diffraction, Scanning Electron Microscopy, and dc magnetization measurement techniques. The frequency dependent microwave absorption measurements have been carried out in the frequency range of 12.4-18 GHz (X and P bands). Diamagnetic and ferromagnetic properties are also investigated. Finally, the microwave absorption of composites is found strongly dependent on the coating time. One absorption peak is observed between 14.3 and 15.8 GHz with an efficient absorption bandwidth of 3.3-4.1 GHz (under -20 dB reflection loss limit). The Reflection loss (RL) can be achieved between -30 and -50 dB. It was found that the RL is decreasing and absorption bandwidth is decreasing with increasing coating time. While absorption peak moves to lower frequencies in Ni coated PAN textile, it goes higher frequencies in Co coated ones. The Ni-Co alloy coated composites have fluctuating curve of absorption frequency with respect to coating time. These results encourage further development of magnetic nanoparticle coated textile absorbers for broadband applications.
|
|
| 3. |
- Altincekic, T. G., et al.
(författare)
-
Synthesis and characterization of CuFe2O4 nanorods synthesized by polyol route
- 2010
-
Ingår i: Journal of Alloys and Compounds. - : Elsevier BV. - 0925-8388 .- 1873-4669. ; 493:1-2, s. 493-498
-
Tidskriftsartikel (refereegranskat)abstract
- Uniform, high quality, CuFe2O4 nanorods with high aspect ratios were synthesized by a surfactant-free single step polyol process at 220 degrees C. The structure of the product was characterized by XRD and FT-IR, and the morphology of the product was analyzed by SEM. The results showed that the as-prepared nanorods have a uniform cross-section and with average diameter of similar to 100 nm and aspect ratio in the range of 13-52. X-ray line profile fitting resulted in crystallite size of 15 nm, which reveals the polycrystalline nature of these nanorods. Magnetic characterization of product was performed by EPR and VSM techniques and the results show that the CuFe2O4 nanorods are ferromagnetic. The line width of the resonance lines in FMR is about 1.8 kOe which may originate from different resonance fields of randomly distributed nanocrystals which have different orientation of magnetic easy axes.
|
|
| 4. |
- Andõn, F. T., et al.
(författare)
-
Biodegradation of Single-Walled Carbon Nanotubes by Eosinophil Peroxidase
- 2013
-
Ingår i: Small. - : Wiley-VCH Verlagsgesellschaft. - 1613-6810 .- 1613-6829. ; 9:16, s. 2721-2729
-
Tidskriftsartikel (refereegranskat)abstract
- Eosinophil peroxidase (EPO) is one of the major oxidant-producing enzymes during inflammatory states in the human lung. The degradation of single-walled carbon nanotubes (SWCNTs) upon incubation with human EPO and H2O 2 is reported. Biodegradation of SWCNTs is higher in the presence of NaBr, but neither EPO alone nor H2O2 alone caused the degradation of nanotubes. Molecular modeling reveals two binding sites for SWCNTs on EPO, one located at the proximal side (same side as the catalytic site) and the other on the distal side of EPO. The oxidized groups on SWCNTs in both cases are stabilized by electrostatic interactions with positively charged residues. Biodegradation of SWCNTs can also be executed in an ex vivo culture system using primary murine eosinophils stimulated to undergo degranulation. Biodegradation is proven by a range of methods including transmission electron microscopy, UV-visible-NIR spectroscopy, Raman spectroscopy, and confocal Raman imaging. Thus, human EPO (in vitro) and ex vivo activated eosinophils mediate biodegradation of SWCNTs: an observation that is relevant to pulmonary responses to these materials. Human eosinophil peroxidase (EPO) is able to degrade SWCNTs in vitro in the presence of H2O2. EPO is one of the major oxidant-generating enzymes present in human lungs during inflammatory states. The biodegradation of SWCNTs is evidenced also in an ex vivo culture system using primary murine eosinophils stimulated to undergo degranulation. These results are relevant to potential respiratory exposure to carbon nanotubes.
|
|
| 5. |
- Avila, Marta, et al.
(författare)
-
Surface functionalized nanofibers for the removal of chromium(VI) from aqueous solutions
- 2014
-
Ingår i: Chemical Engineering Journal. - : Elsevier BV. - 1385-8947 .- 1873-3212. ; 245, s. 201-209
-
Tidskriftsartikel (refereegranskat)abstract
- Polyacrylonitrile (PAN) nanofibers functionalized with amine groups (PAN-NH2) were prepared using a simple one-step reaction route. The PAN-NH2 nanofibers were investigated for the removal of chromium(VI) from aqueous solutions. The adsorption and the kinetic characteristics were evaluated in batch process. The adsorption process showed pH dependence and the maximum Cr(VI) adsorption occurred at pH = 2. The Langmuir adsorption model described well the experimental adsorption data and estimated a maximum loading capacity of 156 mg/g, which is a markedly high value compared to other adsorbents reported. The kinetics studies indicated that the equilibrium was attained after 90 min and the experimental data followed a pseudo-second order model suggesting a chemisorption process as the rate limiting step. X-ray Photoelectron Spectroscopy (XPS) and Fourier transform infrared spectroscopy (FT-IR) revealed that the adsorption of Cr(VI) species on PAN-NH2 was facilitated through both electrostatic attraction and surface complexation. High desorption efficiency (> 90%) of Cr(VI) was achieved using diluted base solutions that may allow the reuse of PAN-NH2 nanofibers.
|
|
| 6. |
- Aydin, M., et al.
(författare)
-
Synthesis, magnetic and electrical characteristics of poly(2-thiophen-3-yl-malonic acid)/Fe(3)O(4) nanocomposite
- 2012
-
Ingår i: Journal of Alloys and Compounds. - : Elsevier BV. - 0925-8388 .- 1873-4669. ; 514, s. 45-53
-
Tidskriftsartikel (refereegranskat)abstract
- Poly(2-thiophen-3-yl-malonic acid)/Fe(3)O(4) nanocomposite was synthesized by the precipitation of Fe(3)O(4) in the presence of poly(2-thiophen-3-yl-malonic acid) (PT3MA). Characterizations of the nanocomposite were performed by XRD, FT-IR, TEM, TGA, AC/DC conductivity and dielectric measurements. The capping of PT3MA around Fe(3)O(4) nanoparticles was confirmed by FTIR spectroscopy, the interaction being between bridging oxygen of the carboxylate and the nanoparticle surface through bidentate binding. The crystallite particle sizes of 6 +/- 3 nm and 7 +/- 3 nm were obtained from XRD line profile fitting and from TEM image analysis respectively, and they are in good agreement with each other. Magnetization measurements revealed that PT3MA coated magnetite particles do not saturate at higher fields. The material showed superparamagnetic character as revealed by the absence of coercivity and remnant magnetization. Magnetic particle size was calculated as 7.3 +/- 1.0 nm from the mean magnetization term in the Langevin function which is also in conformity with the values determined from TEM micrographs and XRD line profile fitting. The TEM particle size analysis of the nanoparticles revealed the presence of a slightly modified magnetically dead nanoparticle surface. AC and DC conductivity measurements were performed to elucidate the electrical conduction characteristics of the product.
|
|
| 7. |
- Battiston, S., et al.
(författare)
-
Synthesis and Characterization of Al-Doped Mg2Si Thermoelectric Materials
- 2013
-
Ingår i: Journal of Electronic Materials. - New York : Springer. - 0361-5235 .- 1543-186X. ; 42:7, s. 1956-1959
-
Tidskriftsartikel (refereegranskat)abstract
- Magnesium silicide (Mg2Si)-based alloys are promising candidates for thermoelectric (TE) energy conversion for the middle to high range of temperature. These materials are very attractive for TE research because of the abundance of their constituent elements in the Earth's crust. Mg2Si could replace lead-based TE materials, due to its low cost, nontoxicity, and low density. In this work, the role of aluminum doping (Mg2Si:Al = 1:x for x = 0.005, 0.01, 0.02, and 0.04 molar ratio) in dense Mg2Si materials was investigated. The synthesis process was performed by planetary milling under inert atmosphere starting from commercial Mg2Si pieces and Al powder. After ball milling, the samples were sintered by means of spark plasma sintering to density > 95%. The morphology, composition, and crystal structure of the samples were characterized by field-emission scanning electron microscopy, energy-dispersive spectroscopy, and x-ray diffraction analyses. Moreover, Seebeck coefficient analyses, as well as electrical and thermal conductivity measurements were performed for all samples up to 600A degrees C. The resultant estimated ZT values are comparable to those reported in the literature for these materials. In particular, the maximum ZT achieved was 0.50 for the x = 0.01 Al-doped sample at 600A degrees C.
|
|
| 8. |
- Baykal, A., et al.
(författare)
-
Acid Functionalized Multiwall Carbon Nanotube/Magnetite (MWCNT)-COOH/Fe3O4 Hybrid : Synthesis, Characterization and Conductivity Evaluation
- 2013
-
Ingår i: Journal of Inorganic and Organometallic Polymers and Materials. - : Springer Science and Business Media LLC. - 1574-1443 .- 1574-1451. ; 23:3, s. 726-735
-
Tidskriftsartikel (refereegranskat)abstract
- A functionalized multiwall carbon nanotube (MWCNT)-COOH/Fe3O4 hybrid was fabricated by co-precipitation method. Fe3O4 nanoparticles were stably attached to the surface of carboxyl groups (COOH). The presence of Fe3O4 nanoparticles and their surface conjugation to MWCNT have been confirmed by XRD, TEM and FT-IR techniques. Magnetic evaluation revealed a superparamagnetic character of the hybrid and therefore the attached Fe3O4 nanoparticles. The crystallite size (9 +/- A 3 nm), particle size (9 +/- A 2 nm) and magnetic domain size estimated for Fe3O4 are consistent with each other, which reveal the single crystalline character of the nanoparticles. Electrical conductivity and dielectric behavior have also been characterized by utilizing impedance spectroscopy up to 3 MHz for an isotherm line varying from 293 to 393 K by 10 K steps. Electrical characteristics and its complex dielectric approaches might be elucidated with the existence of a conventional tunneling conduction mechanism of temperature-independency. The AC conductivity of MWCNT-COOH/Fe3O4 hybrid could also be a consequence of the estimations of the universal dynamic response.
|
|
| 9. |
- Baykal, A., et al.
(författare)
-
Effect of ionic liquids on the electrical and magnetic performance of polyaniline-nickel ferrite nanocomposite
- 2013
-
Ingår i: Materials research bulletin. - : Elsevier BV. - 0025-5408 .- 1873-4227. ; 48:2, s. 378-382
-
Tidskriftsartikel (refereegranskat)abstract
- Polyaniline-NiFe2O4 nanofiber composites were successfully synthesized at the interface of water and ionic liquid via in situ polymerization using cetyl trimethylammonium bromide (CTAB) as surfactant. Both TG analysis and FT-IR measurements proved the presence of organic layer on the surface of NiFe2O4 nanoparticles. The influence of 1-butyl-3-methyl-imidazolium bromide [BMIM]Br as ionic liquid on the structure, conductivity and magnetic property of polyaniline-NiFe2O 4-CTAB nanocomposite were studied in detail. The results show that imidazolium-based ionic liquids BMIMBr acts as an anchor agent for the formation of morphology in polyaniline-NiFe2O4-CTAB nanocomposite. Introduction of ionic liquids obviously improves the conductivity but weakens the magnetization of polyaniline-NiFe2O4 nanocomposite.
|
|
| 10. |
- Baykal, A., et al.
(författare)
-
Hydrothermal synthesis of SrFe 12O 19 and its characterization
- 2012
-
Ingår i: Journal of Superconductivity and Novel Magnetism. - : Springer Science and Business Media LLC. - 1557-1939 .- 1557-1947. ; 25:6, s. 2081-2085
-
Tidskriftsartikel (refereegranskat)abstract
- We have synthesized strontium hexaferrite particles in an alkaline medium using a hydrothermal process at 180°C. Crystalline phase of samples were determined by XRD and spectroscopic, morphological, and magnetic investigation of the sample were FT-IR, SEM, and TG analysis, respectively. XRD analysis revealed few impurity phases in the as-made powder; upon calcinations, the material is converted to desired hexaferrite phase. As synthesized powder exhibits agglomerates with rather smooth facets, in the form of thick platelets. Upon calcination, all these structures were observed to transfer to rod-like structures. The As calcined sample has high specific saturation magnetization (Ms ) values of 65 emu/g that is close to its theoretical value of 74.3 emu/g but the hydrothermally synthesized sample does not. This is in agreement with the observations from XRD analysis where few impurity phases observed in the as-made powder cause a weak magnetic response. Upon calcination, the material is converted to a desired hexaferrite phase with better magnetic properties.
|
|