- Hirai, T., et al.
(författare)
-
Performance and erosion of a tungsten brush limiter exposed at the TEXTOR tokamak
- 2003
-
Ingår i: Journal of Nuclear Materials. - 0022-3115 .- 1873-4820. ; 313, s. 67-71
-
Tidskriftsartikel (refereegranskat)abstract
- To examine the performance of a castellated structure under plasma loading, a hemispherical solid tungsten brush limiter was exposed to the plasma in the TEXTOR-94 tokamak. Due to the thermally isolated column of W segments, IR camera showed a non-uniform temperature distribution. The maximum incident power density was calculated to be about 35-40 MW/m(2). Concerning impurity generation, the structure did not show any particular effects. During plasma exposure, only some minor cracks developed in one of the columns, however, the crack propagation was interrupted by a groove. It can be concluded that the W brush limiter had comparable performance and superior mechanical behaviour compared to a solid W limiter. To study erosion and long-range transport of W atoms, a graphite limiter was exposed simultaneously with the brush limiter. As a result, the deposited W atoms via long-range transportation were estimated to be 10(15) cm(-2) shot(-1) at 46.5 cm from the plasma centre of TEXTOR.
|
|
| 4. |
- Huber, A., et al.
(författare)
-
Comparison of impurity production, recycling and power deposition on carbon and tungsten limiters in TEXTOR-94
- 2001
-
Ingår i: Journal of Nuclear Materials. - 0022-3115 .- 1873-4820. ; 290, s. 276-280
-
Tidskriftsartikel (refereegranskat)abstract
- Impurity production, hydrogen recycling and power deposition on carbon and tungsten limiters have been investigated in TEXTOR-94 using a C-W twin test limiter. Considerable differences have been observed on W and C surfaces, which can be explained by the different particle and energy reflection coefficients of hydrogen on these surfaces. The measurements show in addition that the majority of the carbon release is from recycled carbon and that only a small part (below 10%) is due to net-erosion from the bulk carbon material. The heat deposition on C and W sides differs under the same plasma conditions significantly and is typically about 30% larger on the cal bon surface. The behaviour of the impurity production: recycling and power deposition for various discharge conditions is presented.
|
|
| 5. |
- Ohya, K., et al.
(författare)
-
Simulation study of carbon and tungsten deposition on W/C twin test limiter in TEXTOR-94
- 2000
-
Ingår i: Journal of Nuclear Materials. - 0022-3115 .- 1873-4820. ; 283, s. 1182-1186
-
Tidskriftsartikel (refereegranskat)abstract
- In order to investigate the impurity release and surface modification on a W/C twin test limiter, made of a half of W and the other half of C, exposed to the edge plasma of TEXTOR-94, simulation calculations of ion-surface interaction are conducted by a Monte Carlo code. According to the calculations, experimentally observed spatial distributions of WI and CII line intensities around the W side of the limiter can be explained by physical sputtering of W, reflection of bombarding C ions and physical sputtering of implanted C. The CII line emission, resulting from thermal C atoms, around the C side of the limiter is suppressed by deposition of W, and the reflection of C ions from W deposited on C causes the CII intensity to decay more slowly than that from C without the deposition. Bombardment with deuterium edge plasmas, containing impurity W, produces a thick W layer on the C side of the limiter, whereas C implanted in the W side is strongly sputtered due to impact of most constituent D ions.
|
|
| 6. |
- Pospieszczyk, A., et al.
(författare)
-
Operation of TEXTOR-94 with tungsten poloidal main limiters
- 2001
-
Ingår i: Journal of Nuclear Materials. - 0022-3115 .- 1873-4820. ; 290, s. 947-952
-
Tidskriftsartikel (refereegranskat)abstract
- In TEXTOR-93, experiments have been performed with the upper and lower poloidal limiter blocks made of vapour sprayed (VSP) tungsten (about 0.5 mm) deposited on graphite with a rhenium interlayer. A series of discharge conditions have been performed (density scan, scan of the auxiliary heating power, radius scan). There has been found no restriction for operation at any density with auxiliary heating. For Ohmic conditions the same density with testlimiters could be reached. Under siliconized conditions no severe accumulation of tungsten in the plasma centre could be detected. The blocks could in general stand surface temperatures below 1700 K. Most of them survived also temperatures above 3000 K without exfoliation. However, some blocks showed severe damage by melting or exfoliation probably due to insufficient contact of the tungsten layer with the graphite.
|
|
| 7. |
- Tanabe, T., et al.
(författare)
-
Application of tungsten for plasma limiters in TEXTOR
- 2000
-
Ingår i: Journal of Nuclear Materials. - 0022-3115 .- 1873-4820. ; 283, s. 1128-1133
-
Tidskriftsartikel (refereegranskat)abstract
- Three different types of W limiters were exposed in the TEXTOR plasma and the response of the plasma and materials performance of the limiters were investigated. 1. A W bulk limiter operated with preheating above 800 K withstood a plasma heat load of about similar to 20 MW/m(2) for a few seconds with some slight surface melting during the highest heat load shot. However, it was severely damaged when operated at around 500 K. 2. A C/W twin test limiter, half made of bulk W and the other half of graphite (EK-98) gave very useful information on how low- and high-Z materials behave under conditions of simultaneous utilization as PFM such as cross-contamination and the influence of a large mass difference on hydrogen reflection and deposition. 3. Two sets of main poloidal W limiters made of vacuum vapor sprayed (VPS)-W deposited on graphite (IG-430U) with a Re interlayer could absorb about 60% of the total convection heat and the ohmic plasma with a density as high as 5 x 10(13) cm(-3) was sustained. Most of the VPS-W coated limiters tolerated a heal load of similar to 20 MW/m(2). This series of W limiters experiments in TEXTOR has shown that W is applicable as a PFM, if its central accumulation is avoided by NBI and/or ICRH heating. Nevertheless, some concerns still remain, including difficulty of plasma startup, W behavior in higher temperature plasmas, and materials' selection.
|
|
| 8. |
- Tanabe, T., et al.
(författare)
-
Material mixing on W/C twin limiter in TEXTOR-94
- 2000
-
Ingår i: Fusion engineering and design. - 0920-3796 .- 1873-7196. ; 49, s. 355-362
-
Tidskriftsartikel (refereegranskat)abstract
- In order to investigate the effect of mutual contamination between tungsten (W) and carbon
|
|