COATED NANOPOROUS STRUCTURES SUBJECTED TO STRESS RELIEF ANNEALING

• In this study, the mechanical improvement of the platinum coated nanoporous gold is investigated by performing molecular dynamics simulations. The tensile properties of the structure is enhanced by a stress relief annealing which prevents the high stress concentration observed between the coating and the core materials. The annealing process is performed at 500K for 100ps with a heating and cooling rate of 1K/ps. After the annealing process, tensile loading is applied to the coated structure with a strain rate of 0.001ps-1. According to the result of the tensile analysis, the Young’s modulus increases from 12.2 to 15.25 GPa while the yield strength enhances from 584 to 615 MPa.

• In this study, the mechanical improvement of the platinum coated nanoporous gold is investigated by performing molecular dynamics simulations. The tensile properties of the structure is enhanced by a stress relief annealing which prevents the high stress concentration observed between the coating and the core materials. The annealing process is performed at 500K for 100ps with a heating and cooling rate of 1K/ps. After the annealing process, tensile loading is applied to the coated structure with a strain rate of 0.001ps-1. According to the result of the tensile analysis, the Young’s modulus increases from 12.2 to 15.25 GPa while the yield strength enhances from 584 to 615 MPa.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Teknisk mekanik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Applied Mechanics (hsv//eng)

Nyckelord

Coating, Mechanical behavior, Molecular dynamics, Nanoporous, Stress relief annealing

Publikations- och innehållstyp

kon (ämneskategori)

ref (ämneskategori)