Hot corrosion behavior of solution precursor and atmospheric plasma sprayed thermal barrier coatings
-
Ajay, A. (författare)
-
Raja, V. S. (författare)
-
Sivakumar, G. (författare)
-
visa fler...
-
Joshi, Shrikant V., 1960- (författare)
-
visa färre...
- Elsevier Ltd, 2015
- 2015
- Engelska.
-
Ingår i: Corrosion Science. - : Elsevier Ltd. - 0010-938X .- 1879-0496. ; 98, s. 271-279
- Relaterad länk:
-
https://urn.kb.se/re...
Abstract
Ämnesord
Stäng
- Hot corrosion behavior of solution precursor plasma spray (SPPS) thermal barrier coating (TBC) in molten salt mixtures of 90wt.% Na2SO4+5wt.% V2O5+5wt.% NaCl and 50wt.% Na2SO4+50wt.% V2O5 at 900°C is compared vis-à-vis atmospheric plasma spray (APS) coating. APS TBCs show better hot corrosion resistance than SPPS TBCs in both the salt mixtures. The vertical cracks in SPPS coatings, meant for strain tolerance and high thermal cycling life, serve as channels for transporting salts across the coating to bond coat/top coat interface and accelerate failure. © 2015 Elsevier Ltd.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Ceramic
- Hot corrosion
- SEM
- Superalloys
- XRD
- Coatings
- Corrosion
- Corrosion resistance
- Corrosive effects
- Mixtures
- Plasma jets
- Plasma spraying
- Salt deposits
- Sprayed coatings
- Surface plasmon resonance
- A. Ceramic
- Atmospheric plasma spray
- Atmospheric plasmas
- Hot corrosion resistance
- Molten salt mixtures
- Thermal barrier coating (TBC)
- Thermal barrier coatings
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas