Kinetics of Reduction of NiO-WO3 Mixtures by Hydrogen
-
- Ahmed, Hesham M. (författare)
- KTH,Materialens processvetenskap,Department of Materials Science and Engineering, Royal Institute of Technology
-
- El-Geassy, A. H. A. (författare)
- Central Metallurgical Research and Development Institute (CMRDI), Helwan, Cairo
-
- Seetharaman, Seshadri (författare)
- KTH,Materialens processvetenskap,Kungliga tekniska högskolan, KTH
-
(creator_code:org_t)
- 2009-09-29
- 2010
- Engelska.
-
Ingår i: Metallurgical and materials transactions. B, process metallurgy and materials processing science. - : Springer Science and Business Media LLC. - 1073-5615 .- 1543-1916. ; 41:1, s. 161-172
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- The kinetics of reduction of the oxide mixtures of Ni-W with different Ni/(Ni-W) molar ratios within the range of 923 K to 1173 K in flowing hydrogen gas was investigated by means of thermogravimetric analysis under isothermal conditions. The products were examined by X-ray diffraction, scanning electron microscope (SEM), and electron dispersion spectroscopy (EDS) analyses. Five different oxide mixtures apart from the pure oxides were studied in the present work. The results indicate that the reduction reaction proceeds through three consecutive steps that are as follows: NiO-WO3 -> Ni-WO3 -> Ni-WO2 -> Ni-W From the experimental results, the Arrhenius activation energies of the three steps were evaluated for all of the studied compositions. The activation energy for the first step was calculated to be approximately 18 kJ/mol. For the second and third stages, the activation energy values varied from 62 to 38 kJ/mol for the second stage and 51 to 34 kJ/mol for the third stage depending on the Ni/(Ni + W) molar ratio in the precursors; the activation energy increased with increasing ratios. SEM images showed that the grain size of the final product was dependent on the Ni/(Ni + W) molar ratio; smaller grains were formed at higher nickel contents.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- nickel oxide
- alloys
- tungstate
- gas
- Materials science
- Teknisk materialvetenskap
- Process Metallurgy
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas