Solubility limit and precipitate formation in Al-doped 4H-SiC epitaxial material

• Heavily Al-doped 4H-SiC structures have been prepared by vapor phase epitaxy. Subsequent anneals have been carried out in an Ar atmosphere in a rf-heated furnace between 1500 degreesC and 2000 degreesC for 0.5 to 3 h. Secondary ion mass spectrometry has been utilized to obtain Al concentration versus depth as well as lateral distributions (ion images). Transmission electron microscopy (TEM) has been employed to study the crystallinity and determine phase composition after heat treatment. A solubility limit of similar to 2x10(20) Al/cm(3) (1900 degreesC) is extracted. Three-dimensional ion images show that the Al distribution does not remain homogeneous in layers heat treated at 1700 degreesC or above when the Al concentration exceeds 2x10(20) cm(-3). Al-containing precipitates are identified by energy-filtered TEM.

Nyckelord

silicon-carbide

chemical interaction

phase-equilibria

si-c

aluminum

system

TECHNOLOGY

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)