Alkali-Stable Anion Exchange Membranes Based on Poly(xanthene)
-
- Pan, Dong (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Chen, Si (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Jannasch, Patric (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,LTH profilområde: Energiomställningen,LTH profilområden,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH,LTH Profile Area: The Energy Transition,LTH Profile areas,Faculty of Engineering, LTH
-
(creator_code:org_t)
- 2022-12-20
- 2023
- Engelska 6 s.
-
Ingår i: ACS Macro Letters. - : American Chemical Society (ACS). - 2161-1653. ; 12:1, s. 20-25
- Relaterad länk:
-
http://dx.doi.org/10... (free)
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Poly(xanthene)s (PXs) carrying trimethyl ammonium, methylpiperidinium and quinuclidinium cations were synthesized and studied as a new class of anion exchange membranes (AEMs). The polymers were prepared in a superacid-mediated polyhydroxyalkylation involving 4,4’-biphenol and 1-bromo-3-(trifluoroacetylphenyl)-propane, followed by quaternization reactions with the corresponding amines. The architecture with a rigid PX backbone decorated with cations via flexible alkyl spacer chains resulted in AEMs with high ionic conductivity, thermal and chemical stability. For example, hydroxide conductivities up to 129 mS cm−1 were reached at 80 °C, and all the AEMs showed exceptional alkaline stability with less than 4% ionic loss after treatment in 2 M aq. NaOH at 90 °C during 720 h. Critically, the diaryl ether links of the PX backbone remained intact after the harsh alkaline treatment, as evidenced by both 1H NMR spectroscopy and thermogravimetry. Our combined findings suggest that PX AEMs are viable for application in alkaline fuel cells and electrolyzers.
Ämnesord
- NATURVETENSKAP -- Kemi -- Polymerkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Polymer Chemistry (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Polymerteknologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Polymer Technologies (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas